The invention belongs to the technical field of titanium slag smelting, and mainly relates to a pretreatment method of titanium concentrate. The technical problem to be solved in the invention is to remove the S from the titanium concentrate, so that the titanium concentrate can be used as the raw material for smelting titanium slag. The technical scheme of the invention to solve the technical problems, including the following steps: titanium concentrate by roasting after grading, particle size of +200 to use as the material directly for smelting titanium slag materials; particle size 200 objective material ball, the ball is used as raw material for smelting titanium slag after drying. The method of the invention can remove the S in the titanium concentrate, and the obtained titanium concentrate for smelting titanium slag has advantages to the environment.
【技术实现步骤摘要】
一种钛精矿的预处理方法
本专利技术属于钛渣冶炼
，主要涉及一种钛精矿的预处理方法。主要涉及对含S较高钛精矿进行预处理。
技术介绍
近年来，随着国家对环保不断重视起来，选择一种清洁、环保的工艺，是未来企业发展必然趋势。钛精矿主要用于硫酸法钛白和钛渣冶炼。由于钛渣冶炼对钛精矿需求量远远小于硫酸法钛白需求量，因此优质钛精矿优先销售给钛白企业，这势必影响钛渣冶炼对钛精矿供应。为此，钛渣冶炼企业通常会选用一些劣质钛精矿进行冶炼钛渣，例如S含量较高钛精矿。由于S含量较高钛精矿直接入炉冶炼钛渣会带来以下几个问题，①烟气中SO2含量超标，②渣铁分离不好，③冶炼时间长，④持续泡沫渣时间长，⑤出铁温度高，⑥副产品生铁中S含量较高销售困难，这一系列问题严重影响企业正常生产。
技术实现思路
本专利技术提供了一种钛精矿的预处理方法。该方法能够脱除钛精矿中绝大部分的S，从而减少后续冶炼钛渣时S对工序流程的影响，具有对环境有利等优点。本专利技术提供了一种钛精矿的预处理方法。该方法包括以下步骤：钛精矿经氧化焙烧后分级，粒度+200目的物料直接收集用作冶炼钛渣原料；粒度-200目的物料进行造球，...
【技术保护点】
钛精矿的预处理方法，其特征在于：包括以下步骤：钛精矿经氧化焙烧后分级，粒度+200目的物料直接收集用作冶炼钛渣原料；粒度‑200目的物料进行造球，所得生球干燥后用作冶炼钛渣原料。
【技术特征摘要】
1.钛精矿的预处理方法，其特征在于：包括以下步骤：钛精矿经氧化焙烧后分级，粒度+200目的物料直接收集用作冶炼钛渣原料；粒度-200目的物料进行造球，所得生球干燥后用作冶炼钛渣原料。2.根据权利要求1所述的钛精矿的预处理方法，其特征在于：所述钛精矿来自钒钛磁铁矿选铁尾矿。3.根据权利要求1或2所述的钛精矿的预处理方法，其特征在于：所述钛精矿主要成分为：TiO244.5～46.5％，S0.3～1.2％。4.根据权利要求1～3任一项所述的钛精矿的预处理方法，其特征在于：所述氧化焙烧温度为950～1050℃，时间为0.5～1h。5.根据权利要求1～3任一项所述的钛精矿的预处理方法，...
【专利技术属性】
技术研发人员：李凯茂，韩可喜，肖军，
申请(专利权)人：攀钢集团研究院有限公司，
类型：发明
国别省市：四川,51