The invention relates to the field of material, in particular, an epoxide soybean oil and a preparation method. A method for preparing epoxy soybean oil, which includes: soybean oil and hydrogen peroxide are prepared by epoxide ring - forming reaction catalyzed by solid superacid catalyst. Using solid superacid as catalyst, without generating ring oxidizing agent, hydrogen peroxide can be used directly, the epoxidation of soybean oil in catalytic amount of solid superacid; epoxidation of soybean oil obtained better thermal stability, not easy to decomposition or degeneration, is very conducive to high value of epoxy soybean oil preparation.
【技术实现步骤摘要】
一种环氧大豆油及其制备方法
本专利技术涉及材料领域，具体而言，涉及一种环氧大豆油及其制备方法。
技术介绍
环氧植物油脂增塑剂是一种国际通用的环保增塑剂产品，能够通过国际SGS环保认证和国际REACH安全认证。这类产品无毒且色泽浅，应用范围更广，可以在透明的PVC制品中添加使用，且与PVC制品兼容性好，表现出优良的增塑性能和耐旋光性、耐拉伸、耐老化、阻燃等优良特性。而且环氧植物油增塑剂能与聚酯类增塑剂联用，对减少聚酯的迁移性有明显的协同效应，与有机金属盐稳定剂有协同效应，并用时可减少有机金属盐的用量，进一步降低产品成本。环氧植物油脂增塑剂产品投放市场，具有良好的应用前景。目前，环氧大豆油生产方法主要有溶剂法和无溶剂法。溶剂法由于所用溶剂为苯及苯的同系物，污染环境、生产流程长、三废处理量大、产品质量差，已基本被淘汰。无溶剂法主要工艺是以甲酸或乙酸在催化剂作用下与双氧水反应生成环氧化剂，然后在某一温度范围内将环氧化剂滴加到大豆油中，反应完毕后经碱洗、水洗、减压蒸馏、最后得到产品。该法生产流程短、反应温度低、反应时间短、副产物少、产品质量高，已基本代替溶剂法的生产工艺。虽...
【技术保护点】
一种环氧大豆油的制备方法，其特征在于，包括：大豆油与双氧水在固体超强酸催化剂催化下环氧成环反应制得。
【技术特征摘要】
1.一种环氧大豆油的制备方法，其特征在于，包括：大豆油与双氧水在固体超强酸催化剂催化下环氧成环反应制得。2.根据权利要求1所述的环氧大豆油的制备方法，其特征在于，所述固体超强酸选自SO42-/ZrO2-TiO2、SO42-/ZrO2-Fe2O3-Cr2O3和SO42-/ZrO2-Fe2O3-MnO2中的一种或多种。3.根据权利要求1所述的环氧大豆油的制备方法，其特征在于，包括：将所述固体超强酸与所述大豆油的混合物加热至60-80℃后，保温20-40min，然后滴加所述双氧水，滴加时间为2-5h，滴加完后保温反应7-10h，再降至室温，真空脱水制得环氧大豆油。4.根据权利要求3所述的环氧大豆油的制备方法，其特征在于，所述固体超强酸与所述大豆油的质量比为1:0.001-0.009。5.根据权利要求1所述的环氧大豆油的制备方法，其特征在于，包括：将...
【专利技术属性】
技术研发人员：林跃华，郑晓娜，龙清平，李吉昌，韩淑琴，李平辉，聂建华，马鹏常，徐春涛，
申请(专利权)人：中山职业技术学院，
类型：发明
国别省市：广东,44
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。