A catalyst for acetic acid and the preparation method of one step method of ethanol, the catalyst comprises the following components: active metal additive metal 25 ~ 60wt%, 1 ~ 10wt%, 35 ~ 70wt%, the carrier, the active metal nickel, copper or cobalt, molybdenum, titanium and metal additives for at least one lanthanide the element of the carrier is silica or alumina and silica composite. The catalyst prepared by the invention is used for directly preparing acetic acid ethanol reaction, in 2 ~ 3MPa and 250 ~ 280 DEG C showed high hydrogenation activity and selectivity and stability, the conversion rate of acetic acid can reach above 98.6%, the selectivity of ethanol can reach more than 92%, ethanol can reach 400g L space-time yield
【技术实现步骤摘要】
一种用于醋酸一步法制乙醇的催化剂及其制备方法
本专利技术属于工业催化领域，尤其涉及一种用于醋酸一步法制乙醇的催化剂及其制备方法。
技术介绍
乙醇作为一种基本有机化工原料，广泛应用于食品、化工、医药、染料、国防等行业，又是十分重要的清洁能源。乙醇热值较低、汽化潜热较高、抗爆性能好、氧含量高，作为清洁能源还可制造乙醇汽油用于汽车燃料。与普通汽油相比，乙醇汽油以其燃烧更完全、CO排放量较低、燃烧性能与汽油相似等优良特性，被称为21世纪“绿色能源”。中国市场目前乙醇汽油需求约为200万吨/年，业内预计将迎来快速增长，2020年有望达1000万吨/年。乙醇的生产方法有乙烯水合法和粮食发酵法，我国的工业乙醇70％以上以粮食发酵法生产为主，但是随着世界粮食供应紧张，乙醇生产不得不转向以非粮食作物作为原料的发展方向。近几年我国新建醋酸装置陆续投产，国内醋酸产能急剧增加，而醋酸的表观消费量趋于平稳，造成产能严重过剩，醋酸加氢制乙醇工艺，既可以充分利用过剩的醋酸资源，又可以为燃料乙醇的发展提供新的原料来源。醋酸加氢制乙醇工艺主要有醋酸直接加氢技术(一步法，CH3COOH+2H2→C2...
【技术保护点】
一种用于醋酸一步法制乙醇的催化剂，其特征在于，该催化剂包括如下组分：活性金属25～60wt％，助剂金属1～10wt％，载体35～70wt％；其中，所述活性金属为镍、铜或钴，所述助剂金属为钼、钛和镧系元素中的至少一种，所述载体包括90～100wt％二氧化硅、0～10wt氧化铝。
【技术特征摘要】
1.一种用于醋酸一步法制乙醇的催化剂，其特征在于，该催化剂包括如下组分：活性金属25～60wt％，助剂金属1～10wt％，载体35～70wt％；其中，所述活性金属为镍、铜或钴，所述助剂金属为钼、钛和镧系元素中的至少一种，所述载体包括90～100wt％二氧化硅、0～10wt氧化铝。2.根据权利要求1所述的用于醋酸一步法制乙醇的催化剂，其特征在于，所述催化剂各组分的质量百分比为：活性金属35～55wt％，助剂金属1～5wt％，载体40～60wt％。3.根据权利要求1或2所述的用于醋酸一步法制乙醇的催化剂，其特征在于，所述活性金属为铜，助剂金属为镧。4.如权利要求1-3任一项所述的用于醋酸一步法制乙醇的催化剂的制备方法，其特征在于，其包括如下步骤：将活性金属对应盐溶液放入反应罐中，加入碱性物质调溶液pH至12～13；加入载体中的二氧化硅载体后混合均匀，剧烈搅拌1～3h；升温至80～90℃反应12～24h，升温至90～99℃，反应至溶液pH至6.5～6.7，冷却至室温，过滤，洗涤，在100～12...
【专利技术属性】
技术研发人员：王红，郭建水，刘志明，杨显，宋佳，
申请(专利权)人：河南中宏清洁能源股份有限公司，
类型：发明
国别省市：河南,41