一种钙钛矿型臭氧分解催化剂及其制备方法和应用技术
Perovskite type ozone decomposition catalyst, preparation method and application thereof
The invention relates to a perovskite type ozone decomposition catalyst, the active constituent of the catalyst is perovskite LaFeO3 pure or doped with transition metal and structure of the active components of the catalysts for LaMxFe (1 x) O3, where M is a transition metal, 0 = x = 0.2. The present invention using ferric nitrate, lanthanum nitrate, optionally transition metal nitrate and citric acid as raw material, sintering synthesis by sol-gel combustion, after grinding, calcination, load with perovskite phase catalyst, the grain size of the catalyst is 10 100nm, specific surface area of 5 50m
【技术实现步骤摘要】
一种钙钛矿型臭氧分解催化剂及其制备方法和应用
本专利技术涉及空气污染净化领域，具体涉及一种钙钛矿型臭氧分解催化剂及其制备方法和应用。
技术介绍
臭氧是夏季紫外线强时空气中的主要污染物之一。除紫外线辐射产生外，工业生产中用作抗菌剂、消毒剂使用的臭氧的释放以及室内电器例如复印机、扫描仪工作时的高压放电生成也是室内外空气中臭氧污染的主要来源。臭氧对人体健康有较大的危害，我国《环境空气质量标准GB3095-2012》规定一、二级标准分别为1小时均值不大于0.16与0.20mg/m3(约0.08与0.10ppm)，而《室内空气质量标准GB/T18883-2002》则规定室内空气中1小时均值不大于0.16mg/m3。因此需要开发臭氧降解催化剂以缓解空气中的臭氧污染。对于臭氧分解，目前的研究主要集中在使用活性碳或氧化物分子筛负载金属氧化物来处理，上述处理多针对复印机等高压放电设备产生的臭氧(低浓度/高浓度，低湿度)，而用于臭氧处理废水后尾气的处理则较少(高浓度，高湿度)。目前开发的臭氧催化剂多为过渡金属氧化物，以氧化锰、氧化铁系列为主，例如CN102513106A中公开了一种常...
【技术保护点】
一种钙钛矿型臭氧分解催化剂，其特征在于，所述催化剂由活性组分负载在载体上得到；所述催化剂的活性组分为纯相或掺杂过渡金属的钙钛矿型铁酸镧，所述催化剂的活性组分的结构式为LaMxFe(1‑x)O3，其中M为过渡金属，0≤x≤0.2。
【技术特征摘要】
1.一种钙钛矿型臭氧分解催化剂，其特征在于，所述催化剂由活性组分负载在载体上得到；所述催化剂的活性组分为纯相或掺杂过渡金属的钙钛矿型铁酸镧，所述催化剂的活性组分的结构式为LaMxFe(1-x)O3，其中M为过渡金属，0≤x≤0.2。2.如权利要求1所述的催化剂，其特征在于，所述催化剂的载体为多孔陶瓷、金属泡沫或HEPA过滤网中的任意一种；优选地，所述催化剂中活性组分的负载量为0.01-10wt％；优选地，所述过渡金属为Mn、Co、Ni或Cu中的任意一种或至少两种的组合。3.如权利要求1所述的催化剂，其特征在于，所述催化剂的晶粒尺寸为10-100nm；优选地，所述催化剂的比表面积为5-50m2/g。4.如权利要求1-3任一项所述的钙钛矿型臭氧分解催化剂的制备方法，其特征在于，所述方法包括以下步骤：(1)向硝酸铁、硝酸镧、柠檬酸以及任选的过渡金属的硝酸盐的混合溶液中加入氨水调节pH，加热得到凝胶；(2)将步骤(1)中得到的凝胶烘干，然后点燃进行自蔓延燃烧，燃烧结束后冷却，经过研磨得到粉体；(3)对步骤(2)得到的粉体进行热处理，得到活性组分；(4)将步骤(3)得到的活性组分负载在载体上，得到钙钛矿型臭氧分解催化剂。5.如权利...