The invention provides a treatment method and a treatment device for coal slurry gasification waste residue. The processing method comprises the following steps: coal water slurry gasification residue was centrifuged and a slag processing, a slag water content is 40 ~ 45wt%; the primary treatment of slag drying, two grade and two grade slag, slag content is less than 20wt%, dry carbon 35wt%. The processing method provided by this application can remove some of the waste water from the waste residue by centrifugal separation, and then remove the remaining water in the residue by drying process, thus solving the problem of outdoor air drying, polluting environment and energy recycling.
【技术实现步骤摘要】
水煤浆气化废渣的处理方法及处理装置
本专利技术涉及煤化工领域，具体而言，涉及一种水煤浆气化废渣的处理方法及处理装置。
技术介绍
Texaco水煤浆加压气化工艺(简称TCGP)是由美国德士古石油公司开发的。GE德士古(Texaco)水煤浆加压气化技术属于气流床加压气化技术，原料煤经磨制成水煤浆后泵送进气化炉顶部单烧嘴下行制气。原料煤运输、制浆、泵送入炉系统比干粉煤加压气化要简单。单炉生产能力大，目前国际上最大的气化炉日投煤量为2000t，国内已投产的气化炉能力最大为1000t/d。设计中的气化炉能力最大为1600t/d。上述工艺对原料煤适应性较广，气煤、烟煤、次烟煤、无烟煤、高硫煤及低灰熔点的劣质煤、石油焦等均能用作气化原料。但要求原料煤含灰量较低、还原性气氛下的灰熔点低于1300C，灰渣粘温特性好。气化压力从2.5、4.0、6.5到8.5MPa皆有工业性生产装置在稳定长周期运行，装置建成投产后即可正常稳定生产。气化系统的热利用有两种形式，一种是废热锅炉型，可回收煤气中的显热副产高压蒸汽，适用于联合循环发电；另一种是水激冷型，制得的合成气中的水气比高达1.4，适用于...
【技术保护点】
一种水煤浆气化废渣的处理方法，其特征在于，所述处理方法包括：将所述水煤浆气化废渣进行离心分离，得到一级处理渣，所述一级处理渣的含水量为40～45wt％；将所述一级处理渣进行干燥，得到二级处理渣，且所述二级处理渣的含水量小于20wt％，干基含碳量为35wt％。
【技术特征摘要】
1.一种水煤浆气化废渣的处理方法，其特征在于，所述处理方法包括：将所述水煤浆气化废渣进行离心分离，得到一级处理渣，所述一级处理渣的含水量为40～45wt％；将所述一级处理渣进行干燥，得到二级处理渣，且所述二级处理渣的含水量小于20wt％，干基含碳量为35wt％。2.根据权利要求1所述的处理方法，其特征在于，所述干燥过程为将所述一级处理渣在燃气管筒干燥装置中进行烘干。3.根据权利要求2所述的处理方法，其特征在于，所述干燥过程的干燥温度为550～850℃。4.根据权利要求1所述的处理方法，其特征在于，所述干燥过程为将所述一级处理渣在蒸汽管回转干燥装置中进行烘干。5.根据权利要求4所述的...
【专利技术属性】
技术研发人员：雷朝红，王剑锋，李晓艳，李培丰，杨永涛，王海谦，赵建怀，曹建新，张军，赵小转，李民，范海亮，
申请(专利权)人：神华集团有限责任公司，中国神华煤制油化工有限公司，陕西神木化学工业有限公司，
类型：发明