The invention discloses a novel water-based two-component bamboo board latex emulsion, its composition and the specific proportion is: water 100 350 10 100, polyvinyl alcohol, vinyl acetate 10 200, 10 100 acrylate monomer, functional monomer methacrylic acid 3 10, 1 10, 1 reaction type mixed emulsifier 10, initiator 1 10, 1 10 pH stabilizer. The invention also discloses a new method for the preparation of a new water based double component bamboo collage latex emulsion emulsion. The bamboo samples of the water based double component bamboo collage glue conformed to the EU EN204/205, D4 standard, and the finished products were soaked through the JAS cold and hot water in Japan.
【技术实现步骤摘要】
水基型双组份竹拼板胶乳液
本专利技术属于胶黏剂
，特别涉及一种水基型双组份竹拼板胶乳液。
技术介绍
随着竹木加工业、家具制造业新工艺、新品种的发展，对所用的胶黏剂提出了新的要求。利用窄的竹木板料借边面胶合以增加宽度，要求胶黏剂具有良好的耐水性和粘结强度。目前，现有技术中所使用的胶黏剂大部分都是主剂乳液外加固化剂的双组份拼版胶，但由于乳液形成的胶膜缺乏柔韧性，使得拼版后的竹拼板在日光暴晒极端情况下会出现部分端头开裂现象，从而在外力作用下容易导致竹拼板脆性断裂。专利文献CN102086369A公开了一种水基型双组份竹拼板胶乳液，使用乙酸乙烯酯、丙烯酸丁酯等经过乳液聚合，并通过增强剂增强性能，种子聚合型工艺实现了多元化共聚，乳液形成的是“核壳”结构，使共聚乳液获得具有更加优良的性能。通过在配方中加入增强剂和丙烯酸-2-羟丙酯，使产品具有粘结强度高木破率高、浸泡剥离率和煮沸剥离率低等优点。但由于使用十二烷基硫醇、丙烯酸-2-羟丙酯单体等成分具有可燃及毒性，对人畜及环境有害，限制了该拼板胶的清洁生产。专利文献CN105385389A公开了一种环保超耐水双组份拼板胶，该...
【技术保护点】
一种水基型双组份竹拼板胶乳液，其特征在于，按重量份数计，包括如下组分：水100‑350聚乙烯醇10‑100醋酸乙烯酯10‑200丙烯酸酯类单体10‑100功能单体3‑10甲基丙烯酸1‑10反应型混合乳化剂1‑10引发剂1‑10PH稳定剂1‑10。
【技术特征摘要】
1.一种水基型双组份竹拼板胶乳液，其特征在于，按重量份数计，包括如下组分：水100-350聚乙烯醇10-100醋酸乙烯酯10-200丙烯酸酯类单体10-100功能单体3-10甲基丙烯酸1-10反应型混合乳化剂1-10引发剂1-10PH稳定剂1-10。2.一种水基型双组份拼板胶，其特征在于，按质量份数，包括如下组分：权利要求1所述的水基型双组份竹拼板胶乳液50-90%、无机填料1%-30%、pH稳定剂0.1-5%、增塑剂1-5%、防腐剂0.1-3%。3.如权利要求1所述的水基型双组份竹拼板胶乳液或者权利要求2所述的的水基型双组份拼板胶，其特征在于：所述的聚乙烯醇的聚合度为1500-3000，醇解度为85-90；所述的丙烯酸酯类选自丙烯酸甲酯、丙烯酸乙酯、丙烯酸正丁酯、丙烯酸异丁酯、2-甲基丙烯酸甲酯和2-甲基丙烯酸乙酯、丙烯酸-2-羟基乙酯、丙烯酸-2-羟基丙酯、丙烯酸-2-乙氧基乙酯；所述的功能单体选自端羟基聚醚、端氨基聚醚、羟乙基纤维素、水溶性壳聚糖或水溶性多糖中的一种或两种以上混合物。4.如权利要求1所述的水基型双组份竹拼板胶乳液或者权利要求2所述的的水基型双组份拼板胶，其特征在于：所述的反应型混合乳化剂选自马来酸衍生物、烯丙基醚类磺酸盐、烯丙基琥珀酸烷基酯磺酸钠、丙烯酰胺基磺酸盐。5.如权利要求1所述的水基型双组份竹拼板胶乳液或者权利要求2所述的的水基型双组份拼板胶，其特征在于：所述的引发剂可选自无机...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。