The invention discloses a polyvinyl acetate latex and a preparation method, which mainly relates to the field of latex for furniture. The raw materials by weight: 40 to 50 portions of vinyl acetate; polyvinyl alcohol from 2 to 8; 2 to 6 portions of dibutyl phthalate; octanol 0.5 ~ 1.5; ammonium persulfate from 0.03 to 0.08; 0.01 to 0.1 Lei Lazio stain; 30 to 50 parts of water. The beneficial effect of the invention is that it has the covering property, and it can effectively block the underlying color between the wood skin and the substrate, and better adapt to the trend of thinning of the wood skin, and solve the problem of partial color of light colored wood and wood furniture.
【技术实现步骤摘要】
聚乙酸乙烯酯乳胶及其制备方法
本专利技术涉及家具用乳胶领域，具体是聚乙酸乙烯酯乳胶及其制备方法。
技术介绍
随着现代家具的发展，板木结合家具占据了绝大部分的家具份额。在加工生产中，板木结合家具都是采用密度板贴皮技术。其中密度板指的是家具的基本板材，贴皮是指在密度板上粘贴天然木皮，让家具拥有天然木制品纹理。同时，我国既是一个木材生产大国，也是一个木材消费大国。随着我国国民经济的发展和人民生活水平的提高，社会各方面对木材的需求不断上升。据统计，近10年来我国木材消耗总量增长了173％成为全球第二大木材消耗国。与此同时的是木材供应的持续紧张，不但国内林木资源存在总量不足、资源匮乏、生态失衡的问题，进口也因为非洲原木市场货源告急、俄罗斯及东盟市场相继下发原木“禁出令”、北美硬木产区持续减产等原因而造成国际市场原木供应逐渐减少。使我国木材的工序矛盾进一步加剧，对其主要下游产业——家具行业造成严重影响。其中，对于板木结合家具而言，其天然木皮的供应日趋紧张，价格逐步走高，给板木家具的生产加工带来以下发展趋势——即天然木皮的厚度日趋渐薄。传统板木结合家具使用的天然木皮的厚度一般为...
【技术保护点】
聚乙酸乙烯酯乳胶，其特征在于：其原料按重量份数计包括：醋酸乙烯酯40～50份；聚乙烯醇2～8份；邻苯二甲酸二丁酯2～6份；辛醇0.5～1.5份；过硫酸铵0.03～0.08份；雷拉素染色剂0.01～0.1份；水30～50份。
【技术特征摘要】
1.聚乙酸乙烯酯乳胶，其特征在于：其原料按重量份数计包括：醋酸乙烯酯40～50份；聚乙烯醇2～8份；邻苯二甲酸二丁酯2～6份；辛醇0.5～1.5份；过硫酸铵0.03～0.08份；雷拉素染色剂0.01～0.1份；水30～50份。2.根据权利要求1所述聚乙酸乙烯酯乳胶，其特征在于：其原料按重量份数计包括：醋酸乙烯酯45份；聚乙烯醇5份；邻苯二甲酸二丁酯4份；辛醇1份；过硫酸铵0.05份；雷拉素染色剂0.05份；水44.9份。3.根据权利要求1所述聚乙酸乙烯酯乳胶，其特征在于：所述雷拉素染色剂包括雷拉素红、雷拉素黄、雷拉素蓝中的一种或几种。4.根据权利要求1或2所述聚乙酸乙烯酯乳胶，其特征在于：是通过以下方法制得的：步骤1)将邻苯二甲酸二丁酯加入辛醇，混合搅拌溶解得溶液A；步骤2)将温度为60～80℃的水边搅拌边加入聚乙烯醇后，升温至80～100℃，保温至全部溶解后，使溶液温度降至60～75℃，在搅拌条件下加入醋酸乙烯酯和雷拉素染色剂，得溶液B；步骤3)将溶液A加入溶液B中，再加入过硫酸铵，搅拌混合均匀，在60～75℃温度条件下乳液聚合，即得。5.根据权利要求1或2所述聚乙酸乙烯酯乳胶，其特征在于：是通过以下方法制得的：步骤1)将邻苯二甲酸二丁酯加入辛醇，混合搅拌溶解得溶液A；步骤2)将温度为70℃的水边搅拌边加入聚乙烯醇后，升温至90℃，保温至全部溶解后，使溶液温度降至66～69℃，在搅拌条件下加入醋酸乙烯酯和雷拉素...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。