The invention relates to a thermal insulation material, mix by the raw materials with the following weight percentage after curing and magnesium chloride powder: 10 60%; 21 sodium chloride aqueous solution 48%; sodium sulfonate aqueous solution of 9 27% 0.1 5%; silica sol; perlite powder 1 8%; glass fiber powder 1 8%. Compared with the prior art, the utility model has the advantages of: the insulation curing material, its thermal conductivity in 0.05W/ (m, K), good insulation effect, water resistance, fire prevention, environmental protection and halogenation, not easy to deformation, high temperature combustion and does not release harmful fumes, good safety; source the raw material widely, cheap, non-toxic products, after use Recyclable recycling, saving resources; has the advantages of simple structure, convenient installation, no need of laying keel and moistureproof film, reduce labor and construction cost, while its high strength, able to withstand external shocks, not easy to deformation.
【技术实现步骤摘要】
一种隔热保温材料
本专利技术属于材料领域，具体涉及一种隔热保温材料。
技术介绍
目前，在隔热保温材料领域，隔热材料的质量参差不齐。有的隔热材料选料配方不科学，所用原材料成本过高，不同的化工原料互相组合产生的隔热保温效果差异巨大，浪费了热能，增加了产业生产成本，且达不到理想的隔热保温效果。此外，现有技术中较普遍使用的隔热保温材料，如挤塑板、聚苯板、聚乙烯高度发泡等泡沫材料，虽重量轻，保温隔热效果尚可，但普遍存在易燃、毒烟大、耐温性能差、吸水性能差、在潮湿的环境下易霉变等不足。
技术实现思路
本专利技术提供一种隔热保温材料，旨在至少一定程度上克服现有技术中隔热材料存在的不足。本专利技术解决上述技术问题的技术方案如下：一种隔热保温材料，其由以下重量百分比的各原料充分混合后固化而成：氯化镁粉末10-60％；氯化钠水溶液21-48％；磺酸钠水溶液9-27％；硅溶胶0.1-5％；珍珠岩粉末1-8％；玻璃纤维粉末1-8％。具体的，所述氯化钠水溶液中氯化钠的含量为8-15wt％，所述磺酸钠水溶液中磺酸钠的含量为8-20wt％。在上述技术方案的基础上，本专利技术还可以有如下进一步优化选...
【技术保护点】
一种隔热保温材料，其特征在于，由以下重量百分比的各原料充分混合后固化而成：氯化镁粉末10‑60％；氯化钠水溶液21‑48％；磺酸钠水溶液9‑27％；硅溶胶0.1‑5％；珍珠岩粉末1‑8％；玻璃纤维粉末1‑8％。
【技术特征摘要】
1.一种隔热保温材料，其特征在于，由以下重量百分比的各原料充分混合后固化而成：氯化镁粉末10-60％；氯化钠水溶液21-48％；磺酸钠水溶液9-27％；硅溶胶0.1-5％；珍珠岩粉末1-8％；玻璃纤维粉末1-8％。2.根据权利要求1所述的一种隔热保温材料，其特征在于，由以下重量百分比的各原料充分混合后固化而成：氯化镁粉末43％；氯化钠水溶液32.2％；磺酸钠水溶液18％；硅溶胶1.7％；珍珠岩粉末3.4％；玻璃纤维粉末1.7％。3.根据权利要求1所述的一种隔热保温材料，其特征在于，所...
【专利技术属性】
技术研发人员：蒋珂，
申请(专利权)人：瑞庄武汉科技有限公司，
类型：发明
国别省市：湖北,42