一种可渗透反应墙活性材料及其制备方法技术

本发明专利技术公开一种可渗透反应墙活性材料及其制备方法，涉及污染地下水修复领域,适于处理酸性条件下含多种重金属离子废水。所述的可渗透反应墙活性材料，按重量百分比包括以下组分：铝粉20‑40％；铁粉20‑40％；活性炭30‑40％；沸石5‑10％；并且上述各组分之和为100％。本发明专利技术将铝粉、铁粉、活性炭和沸石按特定比例进行混合，在可渗透反应墙负载后，可同时去除酸性水体中多种重金属离子(Cr(VI)、Cd

A permeable reactive wall active material and its preparation method

The invention discloses a permeable reactive wall active material and a preparation method thereof, which relates to the field of polluted groundwater remediation, and is suitable for dealing with various heavy metal ion wastewater under acidic conditions. The permeable reactive barrier active material comprises the following components by weight percent: 20 aluminum 40%; iron 20 40% 30 40%; activated carbon; zeolite 5 10%; and the components and 100%. The aluminum powder, iron powder, activated carbon and zeolite are mixed in a specific proportion. After loading the permeable reactive wall, a variety of heavy metal ions (Cr (VI) and Cd) can be removed at the same time.

【技术实现步骤摘要】
一种可渗透反应墙活性材料及其制备方法
本专利技术涉及污染地下水修复领域，具体地，涉及一种处理酸性条件下含多种重金属离子的污染地下水的可渗透反应墙活性材料及其制备方法。
技术介绍
随着我国城市化进程的加快和工业的迅猛发展，特别是矿产资源的开采、冶炼等环节的不断推进，重金属对地下水的污染日益严重，污染程度不断加剧，由于重金属不能被微生物降解，且具有生物累积性导致地下水重金属污染治理难度非常大。因此对多种重金属污染废水的修复是一个巨大的难题和挑战。可渗透反应墙技术是近年来迅速发展的一种污染地下水的原位修复技术，通过在受污染地下水流经的方向建造由活性材料组成的反应墙，通过活性材料的吸附、沉淀、化学降解或生物降解等作用去除地下水中的污染物。可渗透反应墙技术克服了传统地下水净化方法的许多弊端，具有处理效果好，无需外加动力，节省地面空间，比抽取技术更为经济、便捷等优点。欧美等国已进行了大量该方法的工程研究及试验研究，并已开始投入商业应用，迄今为止在北美和欧洲已经建立安装了200座以上的可渗透反应墙。可渗透反应墙技术在应用中最重要的考虑因素就是它的长期有效性，而如何选取合理有效并且费用低的活性材料更本文档来自技高网...

【技术保护点】
一种可渗透反应墙活性材料，其特征在于，按重量百分比包括以下各组分：

【技术特征摘要】
1.一种可渗透反应墙活性材料，其特征在于，按重量百分比包括以下各组分：2.根据权利要求1所述的可渗透反应墙活性材料，其特征在于，所述铝粉为零价铝，铝粉中Al的含量≥99wt％。3.根据权利要求1所述的可渗透反应墙活性材料，其特征在于，所述铁粉为零价铁，铁粉中Fe的含量≥98wt％。4.根据权利要求1所述的可渗透反应墙活性材料，其特征在于，所述沸石为斜发沸石，沸石中铝硅含量≥95wt％。5.根据权利要求1所述的可渗透反应墙活性材料，其特征在于，所述活性炭的充填密度为0.5-0...