一种活性炭吸附剂制造技术

本发明专利技术公开了一种活性炭吸附剂，由以下按照重量份的原料组成：氯化钙49‑60份、活性炭17‑32份、水12‑15份、膨润土6‑7份、三氧化二铁1‑5份、聚氨酯2‑6份、乳化剂10‑20份、丁酯2‑10份、六次甲基四胺2‑6份。本发明专利技术的优点在于：本发明专利技术中混合吸附剂由于采用了活性炭为基质，大大提高了吸附剂的气体渗透性能以及体积填充量，同时由于填充密度加大，大大改善了吸附剂的传热性能，在同等体积吸附床的条件下，空调工况体积制冷量可以提高35％左右，制冰工况可以将制冷量提高28％左右。

A kind of activated carbon adsorbent

The invention discloses an activated carbon adsorbent, which consists of the following parts by weight of raw materials: 49 calcium chloride 60, 17 activated carbon 32 and water 12 15, bentonite 6 7 copies, 5 copies, 1 Fe2O3 2 polyurethane 6, emulsifier 10 20 2 copies, 10 copies, six butyl methyl amine 6 four 2. The invention has the advantages that: the invention of hybrid adsorbent with activated carbon as matrix, greatly improving the gas adsorbent permeability and volume filling volume, at the same time as the filling density increased, greatly improve the heat transfer performance of the adsorbent in the adsorption bed under the condition of the same volume, the air-conditioning refrigeration volume can increased by about 35%, the quantity of refrigeration of the ice making condition can be improved by about 28%.

【技术实现步骤摘要】
一种活性炭吸附剂
本专利技术涉及一种吸附剂，特别涉及一种活性炭吸附剂。
技术介绍
作为一种以再生能源或者低品位余热驱动的绿色制冷技术，吸附式制热/热泵技术越来越得到人们的关注。目前在吸附式制冷/热泵系统中所应用的吸附剂主要包括物理吸附剂、化学吸附剂以及物理-化学混合吸附剂。化学吸附剂相对于物理吸附剂来讲，具有吸附、解吸量大、制冷以及制热功率大等优点，同时也存在传热差、气体渗透性差以及膨胀现象严重等缺点，为了解决化学吸附剂的这些缺点，目前混合吸附剂的研究已经成为一个热点。
技术实现思路
本专利技术要解决的技术问题是提供一种能够提高传热和传质性能的活性炭吸附剂。为解决上述技术问题，本专利技术的技术方案为：一种活性炭吸附剂，其创新点在于：由以下按照重量份的原料组成：氯化钙49-60份、活性炭17-32份、水12-15份、膨润土6-7份、三氧化二铁1-5份、聚氨酯2-6份、乳化剂10-20份、丁酯2-10份、六次甲基四胺2-6份。进一步的，氯化钙49-60份、活性炭17-32份、水12-15份、膨润土6-7份、三氧化二铁3份、聚氨酯4份、乳化剂15份、丁酯6份、六次甲基四胺4份。本专利技术的优点本文档来自技高网...

【技术保护点】
一种活性炭吸附剂，其特征在于：由以下按照重量份的原料组成：氯化钙49‑60份、活性炭17‑32份、水12‑15份、膨润土6‑7份、三氧化二铁1‑5份、聚氨酯2‑6份、乳化剂10‑20份、丁酯2‑10份、六次甲基四胺2‑6份。

【技术特征摘要】
1.一种活性炭吸附剂，其特征在于：由以下按照重量份的原料组成：氯化钙49-60份、活性炭17-32份、水12-15份、膨润土6-7份、三氧化二铁1-5份、聚氨酯2-6份、乳化剂10-20份、丁酯2-1...

【专利技术属性】
技术研发人员：陈天烨，
申请(专利权)人：江苏科力特环保科技有限公司，
类型：发明
国别省市：江苏,32