The invention discloses a method for stamping electrophoretic coating, comprises the following steps: (1) the stamping parts after cleaning, spraying the surface modified liquid grease, 20 30min, using water to thoroughly clean; (2) the stamping clean to the electrophoretic coating; (3) to press after painting the cleaning liquid for cleaning, drying and processing into finished products, wherein the cleaning liquid to the mass fraction of sodium fluoride and boric acid solution of 3 5%. The surface of the stamping parts obtained by the method provided by the invention is uniform and thicker, and its corrosion resistance and abrasion resistance are more excellent, and the surface of the film is compact, without dryness and pinhole.
【技术实现步骤摘要】
一种冲压件电泳涂装的方法
本专利技术属于冲压件表面处理
，具体涉及一种冲压件电泳涂装的方法。
技术介绍
冲压件是靠压力机和模具对板材、带材、管材和型材等施加外力，使之产生塑性变形或分离，从而获得所需形状和尺寸的工件的成形加工方法。目前，一些冲压件的工作环境十分恶劣，经常遭受砂石的碰击和地面上泥水等污物的浸蚀，为了延长冲压件的使用寿命，开发出了对冲压件进行电泳涂装的方法。电泳涂装是利用外加电场使悬浮于电泳液中的颜料和树脂等微粒定向迁移并沉积于电极之一的基底表面的涂装方法。与以前的浸涂和喷涂相比，虽然电泳涂装处理后的冲压件表面性能得到了极大的提成，但是由于电泳涂装的工艺复杂，国内涂装技术良莠不齐，导致涂装件的成品率较低，工件表面常会出现漆膜粗糙、针孔的现象。
技术实现思路
为了解决上述技术问题，本专利技术提供一种冲压件电泳涂装方法。本专利技术是通过以下技术方案实现的。一种冲压件电泳涂装的方法，包括以下操作步骤：（1）将冲压件清洗干净后，表面喷涂除脂改性液，20-30min，采用清水彻底清洗，其中除脂改性液由以下重量份的组分制成：辛二胺26-32份、N-辛基二氨乙基甘...
【技术保护点】
一种冲压件电泳涂装的方法，其特征在于，包括以下操作步骤：（1）将冲压件清洗干净后，表面喷涂除脂改性液，20‑30min，采用清水彻底清洗，其中除脂改性液由以下重量份的组分制成：辛二胺26‑32份、N‑辛基二氨乙基甘氨酸盐酸盐14‑20份、水240‑280份；（2）将清洗干净的冲压件进行电泳涂装，其中阴极电泳涂料由以下重量份的组分制成：ZX‑601玻璃树脂55‑63份、间三氟甲基苯甲酸甲酯14‑16份、4‑三甲基硅基苯乙烯11‑15份、四庚基碘化铵3‑5份、钛酸酯偶联剂2‑6份；（3）对涂装后的冲压件用清洗液洗净后，烘干处理后制得成品，其中清洗液为质量分数为3‑5%的氟硼酸钠溶液。
【技术特征摘要】
1.一种冲压件电泳涂装的方法，其特征在于，包括以下操作步骤：（1）将冲压件清洗干净后，表面喷涂除脂改性液，20-30min，采用清水彻底清洗，其中除脂改性液由以下重量份的组分制成：辛二胺26-32份、N-辛基二氨乙基甘氨酸盐酸盐14-20份、水240-280份；（2）将清洗干净的冲压件进行电泳涂装，其中阴极电泳涂料由以下重量份的组分制成：ZX-601玻璃树脂55-63份、间三氟甲基苯甲酸甲酯14-16份、4-三甲基硅基苯乙烯11-15份、四庚基碘化铵3-5份、钛酸酯偶联剂2-6份；（3）对涂...