The invention belongs to the technical field of superhard materials, polycrystalline cubic boron nitride composite sheet and particularly relates to a high thermal stability and good thermal conductivity and a production method thereof. The method includes 80% to 87% nickel cubic boron nitride particles, 1% 3% aluminum powder, 1% 3% 1% 5% metal niobium and vanadium carbide residue preparation of raw materials for powder formulations, raw materials mixed with 8 15 hours after assembly, in 90 100MPa and 1400 1600 DEG C under the condition of synthesis. The invention adopts the high nickel content of cubic boron nitride particles and tungsten, cobalt, aluminum or aluminum ceramic binder obtained product, nickel plating cubic boron nitride particle size, high thermal conductivity, high concentration, fracture toughness and excellent impact resistance and high chemical inertness, has higher life and heat resistance and thermal stability high speed machining of hardened steel, cast iron, carbon steel, die steel and other difficult to cut materials.
【技术实现步骤摘要】
一种高热稳定性和良好导热性的聚晶立方氮化硼复合片及其生产方法
本专利技术属于超硬材料
，具体涉及一种高热稳定性和良好导热性的聚晶立方氮化硼复合片及其生产方法。
技术介绍
目前，在一些难以切削材料的高速精加工中，如淬火钢、铸铁、碳素钢等，要求刀具加工材料具有高热稳定性和良好的导热性，聚晶金刚石等刀具复合片材料在切削过程中，由于温度过高，很容易发生断裂现象，影响工作效率。立方氮化硼的硬度仅次于金刚石，具有很高的热稳定性和极强的化学稳定性，可以有效代替聚晶金刚石复合片，作为黑色金属的加工刀具的材料。现国内生产聚晶立方氮化硼刀具厂家基本依靠进口西方发达国家的聚晶立方氮化硼复合片材料，价格昂贵。现有的生产工艺基本是；聚晶立方氮化硼层是由下述重量份原料制备的：70～85份的立方氮化硼微粉、10～15份的金属结合剂、5～10份的陶瓷添加剂。其生产方法是按照下述步骤进行的：A、混合均匀；B、将混合料和硬质合金基体装入有盐管屏蔽层隔离的钼杯中，加热、合成。然而，现有工艺生产出的聚晶立方氮化硼复合片的热稳定性和导热性又待进一步提高，故，有进一步研究聚晶立方氮化硼复合片的生产工艺...
【技术保护点】
一种高热稳定性和良好导热性的聚晶立方氮化硼复合片，其特征在于，由下述原料制备而成：80％‑87％的镀镍立方氮化硼颗粒、1％‑3％的铝粉、1％‑3％的金属铌和1％‑5％的碳化钒，余量为硅粉。
【技术特征摘要】
1.一种高热稳定性和良好导热性的聚晶立方氮化硼复合片，其特征在于，由下述原料制备而成：80％-87％的镀镍立方氮化硼颗粒、1％-3％的铝粉、1％-3％的金属铌和1％-5％的碳化钒，余量为硅粉。2.根据权利要求1所述的高热稳定性和良好导热性的聚晶立方氮化硼复合片，其特征在于，所述镀镍立方氮化硼颗粒的径粒为2-4微米。3.根据权利要求1所述的高热稳定性和良好导热性的聚晶立方氮化硼复合片，其特征在于，所述铝粉的径粒小于...
【专利技术属性】
技术研发人员：申建中，
申请(专利权)人：金华中烨超硬材料有限公司，
类型：发明
国别省市：浙江,33