The invention discloses a low cost steel roll primer with alkyd resin, which is composed of 3 ~ 5% C8 ~ C12 ~ 2 fatty acids, 4% alcohols, three yuan 4 ~ 6% with diols, side chain of 10 ~ 12%, 4 ~ 6% diethylene glycol, 6 ~ 8% o phthalic anhydride. 6 ~ 8%, 23 ~ 25% of adipic acid, catalyst, esterification of benzene from 0.05 to 0.1% in 1 ~ 3% and 30 ~ 39% xylene solvent made. After the performance test, the results show that the alkyd resin prepared by the invention has good adhesion, flexibility, acid and alkali resistance, low cost, and better environmental protection, and is easy to popularize and use, and has achieved very good technical results.
【技术实现步骤摘要】
一种成本低的卷钢底漆用醇酸树脂及制备方法
本专利技术涉及一种树脂，具体涉及一种环保性强，成本低廉，性能优越，易推广应用的卷钢底漆用醇酸树脂及制备方法，属于高分子材料
技术介绍
卷材用底漆通常是饱和聚酯树脂和甲醚化的氨基树脂搭配的烤漆体系，要求漆膜与底材、面漆有良好的附着力、柔韧性、耐酸碱性，对耐候性和硬度要求一般。一般卷材底漆用饱和聚酯通过使用间苯、对苯、己二酸、无β氢原子的二元醇和少量三元醇组配，不用苯酐和一元酸，现有技术这种原料的配方成本高，难以推广应用等缺点。卷钢涂料是一种重要的工业涂料，用量大，因此，本专利技术在现有技术的基础之上，通过大量实验筛选，研发出一种附着力、柔韧性、耐酸碱性优，但是成本低廉，更易推广应用的卷钢底漆用醇酸树脂。
技术实现思路
专利技术目的：本专利技术的目的是针对现有技术不足，提供一种环保性强，且附着力、柔韧性和耐酸碱性优，但是成本低廉，更易推广应用的卷钢底漆用醇酸树脂；本专利技术另一个目的是提供该成本低的卷钢底漆用醇酸树脂的制备方法。技术方案，为实现以上目的，本专利技术采用的技术方案是：一种成本低的卷钢底漆用醇酸树脂，它由下列...
【技术保护点】
一种成本低的卷钢底漆用醇酸树脂，其特征在于，它由下列质量百分比的原料制成：3～5％的C8～C12的脂肪酸、2～4％的三元醇、4～6％带侧链的二元醇、10～12％的二乙二醇、4～6％的邻二元醇、6～8％苯酐、6～8％的己二酸、23～25％的对苯、0.05～0.1％的酯化催化剂、1～3％的二甲苯、30～39％有机溶剂。
【技术特征摘要】
1.一种成本低的卷钢底漆用醇酸树脂，其特征在于，它由下列质量百分比的原料制成：3～5％的C8～C12的脂肪酸、2～4％的三元醇、4～6％带侧链的二元醇、10～12％的二乙二醇、4～6％的邻二元醇、6～8％苯酐、6～8％的己二酸、23～25％的对苯、0.05～0.1％的酯化催化剂、1～3％的二甲苯、30～39％有机溶剂。2.根据权利要求1所述的成本低的卷钢底漆用醇酸树脂，其特征在于，C8～C12的脂肪酸为辛酸、异辛酸、壬酸、癸酸、十一酸、十二酸中的一种或几种混合物。3.根据权利要求1所述的成本低的卷钢底漆用醇酸树脂，其特征在于，所述的三元醇为甘油、三羟甲基丙烷或三羟甲基乙烷中的一种或几种混合物。4.根据权利要求1所述的成本低的卷钢底漆用醇酸树脂，其特征在于，所述的带侧链的二元醇为甲基丙二醇、新戊二醇、2～乙基～2～丁基丙二醇中的一种或几种混合物。5.根据权利要求1所述的成本低的卷钢底漆用醇酸树脂，其特征在于，所述的邻二元醇为乙二醇、1、2-丙二醇或1、2-丁二醇中的一种或几种混合物。6.根据权利要求1所述的成本低的卷钢底漆用醇酸树脂，其特征在于，所述酯化催化剂为二丁基锡、辛酸亚...
【专利技术属性】
技术研发人员：杨森，惠正权，
申请(专利权)人：江苏三木化工股份有限公司，江苏三木集团有限公司，
类型：发明
国别省市：江苏,32