一种具有超平釉面且无釉面缺陷的陶瓷砖及其制备工艺制造技术
A ceramic tile with super flat glaze and no glaze defect and its preparation technology
A super flat glazed and non glazed ceramic tile defect and its preparation process, wherein the ceramic brick bottom-up comprises the body and glaze layer, pattern layer, isolation layer and the transparent glaze layer, the isolation layer comprises of waterborne tackifying resin by screen printing and printing paste viscosity; the printing paste is 2000 ~ 3000MPa.S; the present invention has ceramic tile glaze and glaze ultra flat without defects, high flatness and its glaze glaze pattern clear and delicate, effectively solves the defects of glaze glaze pouring orange peel, pinhole and hollow glaze.
【技术实现步骤摘要】
一种具有超平釉面且无釉面缺陷的陶瓷砖及其制备工艺
本专利技术涉及建筑陶瓷
，尤其涉及一种具有超平釉面且无釉面缺陷的陶瓷砖及其制备工艺。
技术介绍
目前在深色陶瓷砖产品的生产过程中，其颜色往往限制着其生产，由于现有的喷墨墨水颜色无法满足喷墨生产，因此现有通常是采用喷墨加丝网印花技术相结合来进行砖面的图案装饰，但由于其砖面油性的墨水量或者花釉量较大，在进行淋釉时，其油性的墨水或花釉与水性釉浆往往会形成油、水相互排斥的现象，从而产生瓷砖釉面的橘皮、针孔和凹釉等缺陷，釉面的平整度低，并且导致严重降低深色陶瓷砖的釉面图案的发色效果、清晰度低、色差较大。
技术实现思路
本专利技术的目的在于提出一种具有超平釉面且无釉面缺陷的陶瓷砖，其釉面平整度高且釉面图案清晰细腻。本专利技术的另一目的在于提出一种具有超平釉面且无釉面缺陷的陶瓷砖的制备工艺。为达此目的，本专利技术采用以下技术方案：一种具有超平釉面且无釉面缺陷的陶瓷砖，其由下自上依次包括坯体、底釉层、图案层、隔离层和透明釉层，所述隔离层由含有水性增粘树脂的印膏采用丝网印刷而成；所述印膏的粘度为2000～3000MPa.S。本专利...
【技术保护点】
一种具有超平釉面且无釉面缺陷的陶瓷砖，其由下自上依次包括坯体、底釉层、图案层、隔离层和透明釉层，其特征在于：所述隔离层由含有水性增粘树脂的印膏采用丝网印刷而成；所述印膏的粘度为2000～3000MPa.S。
【技术特征摘要】
1.一种具有超平釉面且无釉面缺陷的陶瓷砖，其由下自上依次包括坯体、底釉层、图案层、隔离层和透明釉层，其特征在于：所述隔离层由含有水性增粘树脂的印膏采用丝网印刷而成；所述印膏的粘度为2000～3000MPa.S。2.根据权利要求1所述的一种具有超平釉面且无釉面缺陷的陶瓷砖，其特征在于：所述印膏还包括氧化锌，所述印膏按照质量百分比，包括如下原料成分：8～12％水性增粘树脂、3～6％乙二醇、2～5％氧化锌、2％防粘网剂和80～85％水。3.根据权利要求2所述的一种具有超平釉面且无釉面缺陷的陶瓷砖，其特征在于：所水性增粘树脂为转性松香树脂或丙烯酸脂中的任意一种。4.根据权利要求2所述的一种具有超平釉面且无釉面缺陷的陶瓷砖，其特征在于：所述防粘网剂为含有活性基团的有机硅聚合物。5.根据权利要求1所述的一种具有超平釉面且无釉面缺陷的陶瓷砖，其特征在于：所述隔离层的厚度为0.01～0.03mm。6.一种如权利要求1～5中任意一项所述的具有超平釉面且无釉面缺陷的陶瓷砖...
【专利技术属性】
技术研发人员：熊勋旺，江健，李清莲，程志坚，黄焱墉，周燕，杨涛，
申请(专利权)人：佛山市东鹏陶瓷有限公司，广东东鹏控股股份有限公司，丰城市东鹏陶瓷有限公司，
类型：发明
国别省市：广东,44