The invention provides a foam glass suitable for interior decoration and its production process, relates to the technical field of glass, foam glass is suitable for indoor decoration comprises the following raw materials in weight portion: 100 waste glass 110, fly ash 25 45 copies, 6 copies, 2 silica powder foaming agent 7, 5 2 flux 6, stabilizer 1.5, 0.9 surfactant 2.4 6 copies, 3 copies of the 1 release agent and foaming promoter 1 2.4; the production process comprises the following steps: (1) weighing the raw materials, (2) mixing and crushing, melting, (3) (4), foaming (5) annealing. The invention solves the problem that the thermal insulation effect, the sound insulation effect and the strength of the existing foam glass are still to be improved when used for indoor decoration.
【技术实现步骤摘要】
一种适用于室内装修的泡沫玻璃及其生产工艺
本专利技术属于玻璃
，具体涉及一种适用于室内装修的泡沫玻璃及其生产工艺。
技术介绍
泡沫玻璃最早是由美国彼兹堡康宁公司专利技术的，是由碎玻璃、发泡剂、改性添加剂和发泡促进剂等，经过细粉碎和均匀混合后，再经过高温熔化，发泡、退火而制成的无机非金属玻璃材料。它是由大量直径为1-2毫米的均匀气泡结构组成。其中吸声泡沫玻璃为50％以上开孔气泡，绝热泡沫玻璃为75％以上的闭孔气泡，可以根据使用的要求，通过生产技术参数的变更进行调整。由于这种新材料具有防潮、防火、防腐的作用，加之玻璃材料具有长期使用性能不劣化的优点，使其在绝热、深冷、地下、露天、易燃、易潮以及有化学侵蚀等苛刻环境下倍受用户青睐。被广泛用于墙体保温、石油、化工、机房降噪、高速公路吸音隔离墙、电力、军工产品等，被用户称之为绿色环保型绝热材料。但是现有的泡沫玻璃用于室内装修时保温隔热效果、隔音效果和强度均有待提高。
技术实现思路
为了解决现有泡沫玻璃在用于室内装修时保温隔热效果、隔音效果和强度均有待提高的问题，本专利技术的目的是提供一种适用于室内装修的泡沫玻璃及其生产工艺...
【技术保护点】
一种适用于室内装修的泡沫玻璃，其特征在于，包括以下重量份的原料：废平板玻璃100‑110份、粉煤灰25‑45份、硅微粉2‑6份、发泡剂5‑7份、助熔剂2‑6份、稳泡剂0.9‑1.5份、表面活性剂2.4‑6.0份、脱模剂1‑3份和发泡促进剂1‑2.4份。
【技术特征摘要】
1.一种适用于室内装修的泡沫玻璃，其特征在于，包括以下重量份的原料：废平板玻璃100-110份、粉煤灰25-45份、硅微粉2-6份、发泡剂5-7份、助熔剂2-6份、稳泡剂0.9-1.5份、表面活性剂2.4-6.0份、脱模剂1-3份和发泡促进剂1-2.4份。2.根据权利要求1所述的适用于室内装修的泡沫玻璃，其特征在于，包括以下重量份的原料：废平板玻璃105份、粉煤灰35份、硅微粉4份、发泡剂6份、助熔剂4份、稳泡剂1.2份、表面活性剂4.2份、脱模剂2份和发泡促进剂1.7份。3.根据权利要求1所述的适用于室内装修的泡沫玻璃，其特征在于：所述发泡剂为石墨。4.根据权利要求1所述的适用于室内装修的泡沫玻璃，其特征在于：所述助熔剂为二氧化锰。5.根据权利要求1所述的适用于室内装修的泡沫玻璃，其特征在于：所述稳泡剂为磷...
【专利技术属性】
技术研发人员：朱明静，
申请(专利权)人：合肥钢骨玻璃制品有限公司，
类型：发明
国别省市：安徽,34