The present invention provides a method, a preparation of core-shell carriers include: silica sol, aluminum sol and titanium sol, sesbania gum, sodium carboxymethyl cellulose and water mixed by glue; the glue is sprayed on the substrate in the 100 200 c roasting to obtain carrier precursor; the shell layer is coated on the outside of the slurry carrier precursor, and then calcined at a temperature of 300 DEG C 500. In the first substrate preparation of an adhesive layer, increase the surface roughness of substrate, the shell material is easy to fall off from the substrate; selection of limited glue ratio, not only can the effective pore plugging material, and increase the mechanical strength to a certain extent; control of sintering temperature in 300 500 C, the effective guarantee of the crystal shell, increases the surface area of the catalyst.
【技术实现步骤摘要】
一种核壳型载体的制备方法
本专利技术涉及催化剂载体领域，具体涉及一种核壳型载体的制备方法。
技术介绍
随着化工业不断向着环保、节能和高效的方向发展。对催化剂的各项性能要求也不断提高。负载型催化剂以其催化活性高和选择性好而被广泛使用。其中以贵金属为活性组分的负载型催化剂应用最为广泛，特别是在石油化工中，贵金属负载型催化剂以其优异效的催化性能广泛的应用在气体纯化、原料加氢、裂解等工艺中。最常用的制备贵金属负载型催化剂的方法是，将贵金属活性组分通过浸渍、喷涂等方式，直接负载在比表面较大的载体上，然后通过焙烧，最终得到贵金属负载型催化剂。上述制备方法中，由于选用了比表面积较大的载体，而比表面积较大的载体其孔道较为丰富，这样就使得在负载的过程中，会有相当大的部分的贵金属渗入载体内部，而在载体内部的贵金属在催化过程中利用率很低，这样就造成了贵金属的浪费，而贵金属的价格昂贵，大大的增加了生产的成本。针对上述问题，人们对载体做了改进，设计出一种核壳型载体，其是在比表面积小的载体上包覆一层比表面积较大的材料，以此来降低比表面积较大的材料表面孔道的深。γ-Al2O3和TiO2以其比表...
【技术保护点】
一种核壳型载体的制备方法，包括如下步骤：(1)将硅溶胶、铝溶胶、钛溶胶、田菁胶、羧甲基纤维素钠和水混合，得到胶液；(2)将所述胶液喷涂在基材上，在100‑200℃焙烧，得到载体前躯体；(3)将壳层浆液包覆在所述载体前驱体外部，然后在温度300‑500℃下焙烧，得到所述核壳型载体。
【技术特征摘要】
1.一种核壳型载体的制备方法，包括如下步骤：(1)将硅溶胶、铝溶胶、钛溶胶、田菁胶、羧甲基纤维素钠和水混合，得到胶液；(2)将所述胶液喷涂在基材上，在100-200℃焙烧，得到载体前躯体；(3)将壳层浆液包覆在所述载体前驱体外部，然后在温度300-500℃下焙烧，得到所述核壳型载体。2.根据权利要求1所述的制备方法，其特征在于，所述壳层浆液为铝溶胶或钛溶胶。3.根据权利要求1或2所述的制备方法，其特征在于，所述胶液中，SiO2、Al2O3、TiO2、田箐胶、羧甲基纤维素钠和水的质量比为：(0.1-10)：(0.1-10)：(0.1-10)：(0.1-1)：(0.1-1)：100。4.根据权利...
【专利技术属性】
技术研发人员：李新，王春艳，成峻青，
申请(专利权)人：北京三聚环保新材料股份有限公司，
类型：发明
国别省市：北京,11