The invention discloses a special flame retardant electrical equipment sealing ring, composed of the following raw materials in weight portion: 1 calcium propionate 2, TEOS 8 10, three 0.3 hexamethylcyclotrisiloxane siloxane 1, methyl vinyl silicone rubber 100 130, eighteen 0.7 1 saturated carbon amide a, ten polybrominated diphenyl ether 1 2 copies, 2 copies of the CPB1 promoter, antioxidant D2 3, sulfur 0.9 1 copies, 6 copies of 4 styrene, cumene peroxide two 0.01 0.03 copies, 13 copies of chlorinated paraffin 10, fluorine rubber 10 20 copies, 15 chloroprene rubber 25 copies, 3 copies of the 1 phenolic resin. The rubber material of the invention has good hardness and aging resistance, good corrosion resistance, long service life, and superior comprehensive performance.
【技术实现步骤摘要】
一种电气设备专用阻燃密封圈
本专利技术涉及一种电气设备辅助装备领域，具体涉及一种电气设备专用阻燃密封圈。
技术介绍
为了保证电气设备的稳定运行，电气设备表面延伸出的连接线周围需使用密封圈加以固定，防止灰尘进入电气设备中，影响散热，进一步对电气设备的稳定运行造成影响，但是电气设备内部本身含有大量元器件，个别部件发热较高，长时间的辐射会导致密封圈的变形，甚至燃烧，进一步导致元器件的运行受到影响。
技术实现思路
本专利技术的目的在于针对现有技术的不足，现提供一种电气设备专用阻燃密封圈。为解决上述技术问题，本专利技术采用的技术方案为：一种电气设备专用阻燃密封圈，其创新点在于：由下述重量份的原料组成的：丙酸钙1-2份，正硅酸乙酯8-10份，六甲基环三硅氧烷0.3-1份，甲基乙烯基硅橡胶100-130份，饱和十八碳酰胺0.7-1份，十溴联苯醚1-2份，促进剂CPB1-2份，防老剂D2-3份，硫磺0.9-1份，苯乙烯4-6份，过氧化二异丙苯0.01-0.03份，氯化石蜡10-13份，氟橡胶10-20份，氯丁橡胶15-25份，酚醛树脂1-3份。进一步的，由下述重量份的原料组成的：丙酸...
【技术保护点】
一种电气设备专用阻燃密封圈，其特征在于：由下述重量份的原料组成的：丙酸钙1‑2份，正硅酸乙酯8‑10份，六甲基环三硅氧烷0.3‑1份，甲基乙烯基硅橡胶100‑130份，饱和十八碳酰胺0.7‑1份，十溴联苯醚1‑2份，促进剂CPB1‑2份，防老剂D2‑3份，硫磺0.9‑1份，苯乙烯4‑6份，过氧化二异丙苯0.01‑0.03份，氯化石蜡10‑13份，氟橡胶10‑20份，氯丁橡胶15‑25份，酚醛树脂1‑3份。
【技术特征摘要】
1.一种电气设备专用阻燃密封圈，其特征在于：由下述重量份的原料组成的：丙酸钙1-2份，正硅酸乙酯8-10份，六甲基环三硅氧烷0.3-1份，甲基乙烯基硅橡胶100-130份，饱和十八碳酰胺0.7-1份，十溴联苯醚1-2份，促进剂CPB1-2份，防老剂D2-3份，硫磺0.9-1份，苯乙烯4-6份，过氧化二异丙苯0.01-0.03份，氯化石蜡10-13份，氟橡胶10-20份，氯丁橡胶15-25份，酚醛树脂1-3份。2.根据权利要求1所述的一种电气设备专用阻燃密封圈，其特征在于：由下述重量份的原料组成的：丙酸钙1份，正硅酸乙酯8份，六甲基环三硅氧烷0.3份，甲基乙烯基硅橡胶100份，饱和十八碳酰胺0.7-1份，十溴联苯醚1份，促进剂CPB1份，防老剂D2份，硫磺0.9份，苯乙烯4份，过氧化二异丙苯0.01份，氯化石蜡10份，氟橡胶10份，氯丁橡...