The invention discloses a preparation method of compressive fly ash steamed brick, which comprises the following steps: the modified sepiolite, diatomite, fly ash, cement, gypsum, heating mixed wet grinding, heating, adding magnesium powder, foam stabilizing agent mixing, molding, pre heating, autoclaved fly ash by compression autoclaved brick. The modified sepiolite is prepared according to the following process: the epoxy resin is dissolved in anhydrous ethanol, and sepiolite powder, polyvinyl alcohol and water are added to get the modified sepiolite. The invention solves the processing problem of fly ash, fly ash is reduced to the city's pollution, and the use of low pressure steam, greatly reduces the cost of steam, and then save the production cost, reduce energy consumption, while the autoclaved brick has good impermeability, crack resistance, anti drop performance, but also thermal insulation.
【技术实现步骤摘要】
一种抗压粉煤灰蒸压砖的制备方法
本专利技术涉及蒸压砖
，尤其涉及一种抗压粉煤灰蒸压砖的制备方法。
技术介绍
蒸压砖是利用煤矸石、尾矿渣、化工渣或者天然砂、海涂泥等作为主要原料，不经高温煅烧而制造的一种新型墙体材料，也称之为免烧砖。该产品符合中国“保护农田、节约能源、因地制宜、就地取材”的发展建材总方针，目前粉煤灰作为工业发电厂的废渣，其排放量逐年锐增，如何采用粉煤灰制备蒸压砖，并达到抗压抗开裂的性能要求，亟待解决。
技术实现思路
基于
技术介绍
存在的技术问题，本专利技术提出了一种抗压粉煤灰蒸压砖的制备方法，解决了粉煤灰处理问题，减少了粉煤灰给城市带来的污染，而且采用低压蒸汽，大大降低了蒸汽成本，进而节约生产成本、降低能耗，同时所得蒸压砖具有良好的抗渗、抗裂、防脱落性能，还能保温、隔热。本专利技术提出的一种抗压粉煤灰蒸压砖的制备方法，包括如下步骤：将改性海泡石、粉煤灰、硅藻土、水泥、石膏，升温混合湿磨，升温，加入镁粉、稳泡剂搅拌，压制成型，升温预养，蒸压处理得到抗压粉煤灰蒸压砖。优选地，改性海泡石、粉煤灰、硅藻土、水泥、石膏、镁粉、稳泡剂的重量比为60-80：80-...
【技术保护点】
一种抗压粉煤灰蒸压砖的制备方法，其特征在于，包括如下步骤：将改性海泡石、粉煤灰、硅藻土、水泥、石膏，升温混合湿磨，升温，加入镁粉、稳泡剂搅拌，压制成型，升温预养，蒸压处理得到抗压粉煤灰蒸压砖。
【技术特征摘要】
1.一种抗压粉煤灰蒸压砖的制备方法，其特征在于，包括如下步骤：将改性海泡石、粉煤灰、硅藻土、水泥、石膏，升温混合湿磨，升温，加入镁粉、稳泡剂搅拌，压制成型，升温预养，蒸压处理得到抗压粉煤灰蒸压砖。2.根据权利要求1所述抗压粉煤灰蒸压砖的制备方法，其特征在于，改性海泡石、粉煤灰、硅藻土、水泥、石膏、镁粉、稳泡剂的重量比为60-80：80-100：8-16：10-14：6-10：2-4：2-4。3.根据权利要求1或2所述抗压粉煤灰蒸压砖的制备方法，其特征在于，包括如下步骤：按重量份将60-80份改性海泡石、80-100份粉煤灰、8-16份硅藻土、10-14份水泥、6-10...
【专利技术属性】
技术研发人员：梅林，
申请(专利权)人：铜陵丰泽建材科技有限公司，
类型：发明
国别省市：安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。