一种超薄涂料及其制备方法技术

本发明专利技术公开了一种超薄涂料及其制备方法。其主要组成成分及重量配比为：聚氨酯丙烯酸树脂20%‑29%，聚磷酸氨25%‑28%，引发剂1.5%‑3.5%，钛白粉20%‑24%，丙稀酸聚合物0.8%‑1%，氟改性表面活性剂0.5%‑1%，氯化石蜡20.5%‑22.5%，溶剂15%‑20%，中空玻璃微珠3%‑7%。本发明专利技术其提供一种超薄涂料及其制备方法，其主要适合潮湿环境下降低热工设备表面温度流失并减少设备能耗。

Ultra thin coating and its preparation method

The invention discloses an ultra thin coating and a preparation method thereof. The main composition and weight proportion: 20% 29% polyurethane acrylic resin, poly ammonium phosphate 25% 28%, 1.5% 3.5% initiator, titanium dioxide 20% 24%, 0.8% 1% acrylic acid polymer, fluorine modified surfactant 0.5% 1%, 20.5% chlorinated paraffin 22.5%, solvent 15% 20% hollow glass bead 3% 7%. The invention provides an ultra-thin coating and the preparation method thereof, which is mainly suitable for reducing the surface temperature loss of thermal equipment and reducing the energy consumption of the equipment in humid environment.

【技术实现步骤摘要】
一种超薄涂料及其制备方法
本专利技术涉及涂料
，具体为一种超薄涂料及其制备方法。
技术介绍
涂料是一种能牢固覆盖在物体表面起保护、装饰、标志行业，随着经济的不断发展，科学技术的不断进步，其应用领域也越来越广，在一些应用领域，例如热工类设备，其对表面绝热性能有一定的要求，如表面绝热性能较差，则容易造成表面温度较高，尤其造成大量热量流失，因此通过在表面涂上一层具有保温隔热的涂料，便是解决这一问题的有效途径。
技术实现思路
本专利技术的目的在于提供一种超薄涂料及其制备方法，其主要适合潮湿环境下降低热工设备表面温度流失并减少设备能耗。本专利技术所要解决的技术问题采用以下技术方案来实现：一种超薄涂料，其主要组成成分及重量配比为：聚氨酯丙烯酸树脂20%-29%，聚磷酸氨25%-28%，引发剂1.5%-3.5%，钛白粉20%-24%，丙稀酸聚合物0.8%-1%，氟改性表面活性剂0.5%-1%，氯化石蜡20.5%-22.5%，溶剂15%-20%，中空玻璃微珠3%-7%。引发剂：为裂解型引发剂，可吸收紫外光能量，为涂膜提供官能基团所需的能量；钛白粉：赋予涂膜更好的延展性；丙稀酸聚合物：为涂料提供润湿本文档来自技高网...

【技术保护点】
一种超薄涂料，其特征在于，其主要组成成分及重量配比为：聚氨酯丙烯酸树脂20%‑29%，聚磷酸氨25%‑28%，引发剂1.5%‑3.5%，钛白粉20%‑24%，丙稀酸聚合物0.8%‑1%，氟改性表面活性剂0.5%‑1%，氯化石蜡20.5%‑22.5%，溶剂15%‑20%，中空玻璃微珠3%‑7%。

【技术特征摘要】
1.一种超薄涂料，其特征在于，其主要组成成分及重量配比为：聚氨酯丙烯酸树脂20%-29%，聚磷酸氨25%-28%，引发剂1.5%-3.5%，钛白粉20%-24%，丙稀酸聚合物0.8%-1%，氟改性表面活性剂0.5%-1%，氯化石蜡20.5%-22.5%，溶剂15%-20%，中空玻璃微珠3%-7%。2.一种超薄涂料的制备方法，其特征在于，其制备流程主要包括以下步骤：（1）备料：将聚氨酯丙烯酸树脂、聚磷酸氨、引发剂、钛白粉、丙稀酸聚合物、氟改性表面活性剂、氯化石蜡、溶剂和中空玻璃微珠按照上...

【专利技术属性】
技术研发人员：姜阀，孙庆兵，吴瑞华，
申请(专利权)人：安徽康瑞高科新材料技术工程有限公司，
类型：发明
国别省市：安徽,34