本发明专利技术公开了一种低光泽消光粉末涂料，所述低光泽消光粉末涂料由以下质量百分比的组分组成：羟基聚酯树脂54.0‑58.0％，双官能团固化剂3.5‑4.5％，交联剂2.0‑3.0％，流平剂0.8‑1.2％，消泡剂0.40‑0.60％，稳定剂0.40‑0.60％，炭黑0.8‑1.2％，钛白粉30.9‑38.1％。本发明专利技术还公开了一种低光泽消光粉末涂料的制备方法。本发明专利技术的低光泽消光粉末涂料具有低光泽、生产简单、重复性好等方面的优点。

Low gloss extinction powder coating and its preparation method

The invention discloses a low gloss powder coating matting, the low gloss powder coating matting consists of the following components: the mass percentage of hydroxyl polyester resin 54 58%, 3.5 4.5% bifunctional curing agent, crosslinking agent 2 leveling agent 0.8 3%, 1.2%, 0.40 and 0.60% defoaming agent, stabilizer 0.40 0.60% 0.8 1.2%, carbon black, titanium dioxide, 30.9 38.1%. The invention also discloses a preparation method of low gloss extinction powder coating. The low gloss extinction powder coating has the advantages of low gloss, simple production, good repeatability, etc..

【技术实现步骤摘要】
低光泽消光粉末涂料及其制备方法
本专利技术涉及一种低光泽消光粉末涂料及其制备方法，属于涂料

技术介绍
聚氨酯粉末涂料因优越的耐候性和突出的流平和表面性能成为极佳的选择，广泛用于墙面装饰件、车库门、门窗型材和汽车配件等的涂装。相较于液体涂料，配制消光效果的粉末涂料要困难得多，且制备方法也完全不同。液体涂料中的颜填料在涂膜干燥过程中向表面迁移，这些粒子产生的粗糙度足以形成减光效果。粉末涂料不含溶剂，烘烤过程中熔融粘度相对较高，不存在由低黏度液态向固态的转变，且消光剂在涂膜表面的聚焦很少。因此，急需开发一种低光泽、生产简单、重复性好的低光泽消光粉末涂料及其制备方法。
技术实现思路
本专利技术的目的在于提供一种低光泽消光粉末涂料及其制备方法，使低光泽消光粉末涂料具有低光泽、生产简单、重复性好等方面的优点。为解决上述技术问题，本专利技术的低光泽消光粉末涂料，所述低光泽消光粉末涂料由以下质量百分比的组分组成：作为本专利技术的改进，所述低光泽消光粉末涂料由以下质量百分比的组分组成：作为本专利技术的改进，所述双官能团固化剂的两种官能团分别为异氰酸酯基和羧基。作为本专利技术的改进，所述交联剂为羟本文档来自技高网...

【技术保护点】
一种低光泽消光粉末涂料，其特征在于，所述低光泽消光粉末涂料由以下质量百分比的组分组成：

【技术特征摘要】
1.一种低光泽消光粉末涂料，其特征在于，所述低光泽消光粉末涂料由以下质量百分比的组分组成：2.根据权利要求1所述的低光泽消光粉末涂料，其特征在于，所述低光泽消光粉末涂料由以下质量百分比的组分组成：3.根据权利要求1所述的低光泽消光粉末涂料，其特征在于，所述双官能团固化剂的两种官能团分别为异氰酸酯基和羧基。4.根据权利要求1所述的低光泽消光粉末涂料，其特征在于，所述交联剂为羟烷基酰胺交联剂或环氧基交联剂。5.根据权利要求1所述的低光泽消光粉末涂料，其特征在于，所述流平剂为SiO2吸收型，所述消泡剂为安息香，所述稳定剂为位阻胺光稳定剂...