一种无卤阻燃高性能聚碳酸酯工程塑料制造技术

本发明专利技术所述一种无卤阻燃高性能聚碳酸酯工程塑料，其原料及原料重量百分含量如下：树脂40‑50％；聚乙烯醇0.1‑1％；玻璃纤维0.1‑3％；氧化镧0.1‑3％；钛酸四丁酯0.1‑3％；赤铁矿石40‑60％。本发明专利技术将含硫特种工程塑料与含硅阻燃剂配合使用，赋予聚碳酸酯良好的阻燃性能和较高的耐热性，良好的相容性改善了复合材料的力学性能，克服了小分子含硫阻燃剂易析出、吸潮的缺点。

Halogen free flame retardant high performance polycarbonate engineering plastics

The invention relates to a halogen-free flame retardant high performance polycarbonate engineering plastics, as the raw materials and raw materials by weight percent: 40 resin 50%; polyvinyl alcohol 0.1 1% 0.1 3%; glass fiber; lanthanum oxide 0.1 3% four 0.1 3%; butyl titanate; hematite 40 60%. The invention of special engineering plastics with sulfur silicon containing flame retardant, heat resistant polycarbonate with good flame retardant properties and high resistance, improve the mechanical properties of the composite good compatibility, to overcome the small molecules containing flame retardant, moisture absorption to the precipitation of the shortcomings.

【技术实现步骤摘要】
一种无卤阻燃高性能聚碳酸酯工程塑料
本专利技术涉及一种无卤阻燃高性能聚碳酸酯(PC)工程塑料，可应用于卡座、充电器、连接器、液晶面板、热升华打印机、高温线圈骨架和等离子电视散热窗等对耐热和阻燃有很高要求的关键零部件，属于化工新材料

技术介绍
聚碳酸酯(PC)基复合工程塑料是一类性能优良的热塑性树脂基复合材料，具有较高的冲击强度、耐热性和尺寸稳定性，被广泛用作制造各类工业零配件的原材料，如各种电子电器产品的外壳与传动件，办公设备以及其它工业应用领域。这些应用一般都要求材料阻燃同时具有较高的热变形温度，因此对聚碳酸酯(PC)基复合工程塑料进行阻燃及耐热改性就显得十分必要。目前阻燃类聚碳酸酯(PC)基复合工程塑料普遍使用了较多小分子量的磷酸酯类阻燃剂或者以多溴联苯醚和多溴联苯类物质为代表的含卤素阻燃剂。前者分子量较小在常温下呈液态，对聚碳酸酯(PC)基复合工程塑料的耐热性能有较大负面影响，降低了耐热变形温度，而后者由于近年来世界各国对环境保护及人身健康的日益重视，在欧盟RoHS指令等文件中都已明确规定禁止使用。而目前随着科技的发展尤其电力电子行业的日新月异的进步，各种电子元器件朝本文档来自技高网...

【技术保护点】
一种无卤阻燃高性能聚碳酸酯工程塑料，其特征在于，其原料及原料重量百分含量如下：树脂40‑50％；聚乙烯醇0.1‑1％；玻璃纤维0.1‑3％；氧化镧0.1‑3％；钛酸四丁酯0.1‑3％；赤铁矿石40‑60％。

【技术特征摘要】
1.一种无卤阻燃高性能聚碳酸酯工程塑料，其特征在于，其原料及原料重量百分含量如下：树脂40-50％；聚乙...

【专利技术属性】
技术研发人员：赖树兴，
申请(专利权)人：佛山市北朝源科技服务有限公司，
类型：发明
国别省市：广东,44