The invention discloses an anti static, oil proof and anti skid multifunctional safety shoes which belongs to the field of garment manufacturing technology. The sole material comprises the following raw materials in parts by weight: 30 made of latex 50, ethyl butyrate 10 20 copies, 8 copies of clay 5, promoter 5 8 copies, 8 copies of furfural resin 3, tailings powder 1 2, two 3 butyl ether 8, barium sulfate 1 in 2, sulfur 1 2; the vamp material made of canvas coated cold oil proof rubber. The invention of the anti-static oil proof skidproof multifunctional safety shoes, with a new formulation, preparation of safety shoes, wearing comfortable, antistatic ability, oil proof ability, the stain is not easily contaminated, long-term wear in cold conditions, not brittle, long service life, vamp coated cold oil proof rubber not easy to stain.
【技术实现步骤摘要】
一种防静电防油防寒防滑多功能安全鞋
本专利技术属于服装制造
，具体涉及一种防静电防油防寒防滑多功能安全鞋。
技术介绍
采用硫化橡胶工艺制备的安全鞋，具有一定的绝缘功能，韧性好，但是，容易产生静电，不耐油，容易附着污渍，使用寿命短，此外，在低温下长久使用容易变脆，变硬，穿起来变得不舒适。专利CN101569441公开了一种耐油，绝缘，耐酸碱，耐高温多功能安全鞋，其鞋底原料组成为耐油胶，天然胶，炭黑，陶土，硫酸钡，硬脂酸，二丁酯，促进剂，硫磺，凡士林。但是，该鞋底耐寒性能差，在寒冷情况下容易变脆。专利CN102336973公开了一种安全鞋底材料及其制备方法，于它的组分和重量份数如下TPE100份；PS150份；PE111份；米糠70份；二丁醚22份；乙酸乙酯36份；硫代硫酸盐27份；橄榄油18份；丙酮19份，苯胺10份。该鞋底耐油，绝缘，耐寒性能均不佳。
技术实现思路
本专利技术的目的在于提供一种防静电防油防寒防滑多功能安全鞋。一种防静电防油防寒防滑多功能安全鞋，包括鞋底材料和鞋面材料，所述鞋底材料由如下重量份数的原料制成：乳胶30-50份，丁酸乙酯10-20份，陶...
【技术保护点】
一种防静电防油防寒防滑多功能安全鞋，包括鞋底材料和鞋面材料，其特征在于，所述鞋底材料由如下重量份数的原料制成：乳胶30‑50份，丁酸乙酯10‑20份，陶土5‑8份，促进剂5‑8份，糠醛树脂3‑8份，尾矿粉1‑2份，二丁醚3‑8份，硫酸钡1‑2份，硫磺1‑2份；所述鞋面材料由帆布涂覆防寒防油胶制成。
【技术特征摘要】
1.一种防静电防油防寒防滑多功能安全鞋，包括鞋底材料和鞋面材料，其特征在于，所述鞋底材料由如下重量份数的原料制成：乳胶30-50份，丁酸乙酯10-20份，陶土5-8份，促进剂5-8份，糠醛树脂3-8份，尾矿粉1-2份，二丁醚3-8份，硫酸钡1-2份，硫磺1-2份；所述鞋面材料由帆布涂覆防寒防油胶制成。2.根据权利要求1所述防静电防油防寒防滑多功能安全鞋，其特征在于，所述促进剂为促进剂D或促进剂DM。3.根据权利要求1所述防静电防油防寒防滑多功能安全鞋，其特征在于，所述尾矿粉为磷尾矿粉，铁尾矿粉，钼尾矿粉，铜尾矿粉，铝尾矿粉，锡尾矿粉中的一种或一种以上。4.根据权利要求1所述防静电防油防寒防滑多功能安全鞋，其特征在于，所述防寒防油胶涂覆的量为帆布质量的5-15％，由如下重量份数的组分组成：橡胶...