Preparation method of high purity nano selenium
The invention discloses a preparation method of high-purity nanometer selenium. The borohydride salt ethanol solution and mixed powder mixture, adding ethanol and dimethyl carbonate two to form mixed system, to 0~90 deg.c stirring for 2~10h, then add pH regulator to pH value is 5~6.5, adding deionized water to red precipitate, filter to obtain the target materials in high purity nano selenium drying temperature 10~90. The diffraction peaks of any impurity can not be found in the X ray diffraction pattern of the high-purity nano selenium prepared by the invention, and it can be found by the transmission electron microscope that the pure selenium with high purity nanometer selenium in the preparation method of the invention is spherical in shape, and wide in 45~70nm.
【技术实现步骤摘要】
一种高纯纳米硒的制备方法
本专利技术属于微量元素
，具体涉及一种高纯纳米硒的制备方法。
技术介绍
硒是一种化学元素，化学符号是Se，在化学元素周期表中位于第四周期VIA族，是一种非金属。由于硒是动物和人体中一些抗氧化酶（谷胱甘肽过氧化物酶）和硒-P蛋白的重要组成部分，在体内起着平衡氧化还原氛围的作用，研究证明具有提高动物免疫力作用，在国际上硒对于免疫力影响和癌症预防的研究是该领域的热点问题，目前，中国营养学会推荐的成人摄入量为每日50-250微克，而中国2/3地区硒摄入量低于最低推荐值，因此，中国是一个既有丰富硒资源，又存在大面积硒缺乏地区，这也是国际学者对中国感兴趣的原因。据统计，全世界42个国家和地区缺硒，中国有72%的地区处于缺硒和低硒生态环境之中。由于独特的地质地理环境，使得位于秦巴山深处的安康，成为世界上面积最大、富硒地层最厚、最宜开发利用的富硒区，属于中国罕见富硒区。在这一纬度带上的区域被称为中国硒谷。在这一区域生长的植被，含有充足的硒元素，可以满足人们缺硒的需求。补硒已经成为我们追寻健康的一种潮流，也是势在必行的健康使命。通过健康食品进行补硒更...
【技术保护点】
一种高纯纳米硒材料的制备方法，其特征在于是将硼氢化盐的乙醇溶液与硒粉混合，再加入乙醇与碳酸二甲酯的混合物形成混合体系，于温度0~90℃下搅拌反应2~10h，然后加入pH调节剂调至pH值为5~6.5，加入去离子水得红色沉淀，抽滤洗涤后于温度10~90℃烘干即得到目标物高纯纳米硒材料。
【技术特征摘要】
1.一种高纯纳米硒材料的制备方法，其特征在于是将硼氢化盐的乙醇溶液与硒粉混合，再加入乙醇与碳酸二甲酯的混合物形成混合体系，于温度0~90℃下搅拌反应2~10h，然后加入pH调节剂调至pH值为5~6.5，加入去离子水得红色沉淀，抽滤洗涤后于温度10~90℃烘干即得到目标物高纯纳米硒材料。2.根据权利要求1所述的高纯纳米硒材料的制备方法，其特征在于所述的硼氢化盐为硼氢化金属盐中的一种或几种。3.根据权利要求1或2所述的高纯纳米硒材料的制备方法，其特征在于所述的硼氢化盐为硼氢化钠或硼氢化钾。4.根据权利要求1所述的高纯纳米硒材料的制备方法，其特征在于所述的硼氢化盐的乙醇溶液的质量浓度为1~99%。5.根据权利要求1所述的高纯纳米硒材料的制备方法，其特...