一种聚四氟乙烯涂层皮带的焊接方法技术
Welding method of polytetrafluoroethylene coating belt
The welding process of polytetrafluoroethylene coating belt, which is characterized in that the Teflon coated belt ends on the platform flat butt welding; membrane and high strength fiber cloth are tiled in the middle of the belt joint alignment, open a hot iron, temperature is set to 350 400 DEG C, the iron pressing in the welding cloth, 30 50s, removing iron, stainless steel iron box is provided with a water pressure in the welding position of cooling of the 60 90s, remove the stainless steel box, welding and welding cloth belt. The belt seal of the joint is obviously reduced, and the service life is obviously improved.
【技术实现步骤摘要】
一种聚四氟乙烯涂层皮带的焊接方法
本专利技术属于高分子材料
，特别涉及一种聚四氟乙烯涂层皮带的焊接方法。
技术介绍
聚四氟乙烯(PTFE)又称铁氟龙或特氟龙（Teflon），与其他高分子材料相比，因其具有卓越的耐热、阻燃、耐腐蚀性以及超低的摩擦系数，工业上常以玻璃纤维、芳纶纤维编织布为基底，以聚四氟乙烯为涂层，制造用于特殊功能的输送皮带。这种输送皮带具有耐磨、耐高温、耐腐蚀、易清洁的功能，长期使用温度达到260℃。皮带本身根据有没有接缝分为两种，一种为无缝带，一种为普通皮带。无缝皮带为特定尺寸的环状皮带，直接装配在其他设备上使用，不会再产品表面留下接头带来的印痕，在产品表面质量要求高的领域中备受关注，但是与普通皮带相比，其成本高昂，在设备配套安装上也存在很多问题，目前大部分传输皮带都不得不采用带有接头的普通皮带。目前皮带接头材质包含金属的、非金属的，其连接形式有拼接、铰链、对接、重叠等多种形式。但都会在产品表面产生明显的接头印痕。聚四氟乙烯涂层皮带价格昂贵，为了控制成本，皮带使用寿命是行业关注的重点，而聚四氟乙烯涂层皮带损坏，一般都是从最薄弱的位置——皮带接头开始损坏。开发优良的皮带接头方法，不仅需要解决皮带接头印痕的问题，同时必须满足很好的使用寿命，而这个问题也给行业带来了极大挑战。
技术实现思路
为解决上述问题，本专利技术提供了一种聚四氟乙烯涂层皮带焊接工艺，是以氟塑料膜为焊接膜，以聚四氟乙烯涂覆的高强度纤维基布为焊接基布，使用高温熨斗对其加热加压一段时间，然后冷却定型，使焊接基布与皮带焊接到一起。本专利技术的技术方案是通过以下方式实现的：一种聚四氟...
【技术保护点】
一种聚四氟乙烯涂层皮带焊接工艺，其特征在于：取聚四氟乙烯涂层皮带平铺在平台上两头对接；将焊接膜和高强度纤维基布依次平铺在皮带的搭接缝上中间对齐，打开高温熨斗，温度设定为350‑400℃，使熨斗按压在焊接基布上，保持30‑50s，移开熨斗，用装有冷水的不锈钢铁箱压在焊接位置处降温60‑90s，移开不锈钢铁箱，焊接基布与皮带完成焊接。
【技术特征摘要】
1.一种聚四氟乙烯涂层皮带焊接工艺，其特征在于：取聚四氟乙烯涂层皮带平铺在平台上两头对接；将焊接膜和高强度纤维基布依次平铺在皮带的搭接缝上中间对齐，打开高温熨斗，温度设定为350-400℃，使熨斗按压在焊接基布上，保持30-50s，移开熨斗，用装有冷水的不锈钢铁箱压在焊接位置处降温60-90s，移开不锈钢铁箱，焊接基布与皮带完成焊接。2.根据权利要求1所述的一种聚四氟乙烯涂层皮带焊接工艺，其特征在于：所述的聚四氟乙烯涂层皮带的材质为聚...
【专利技术属性】
技术研发人员：朱华平，沃晓剑，史玉龙，
申请(专利权)人：江苏奇一科技有限公司，
类型：发明
国别省市：江苏,32