具有屏蔽作用的导热PBT复合材料及制备方法技术
Thermal conductive PBT composite material with shielding effect and its preparation method
The invention discloses a heat shielding effect of PBT composite material and a preparation method thereof, prepared by the following raw materials in parts by weight: polybutylene terephthalate, aluminum powder, toughening agent, coupling agent, antioxidant, heat stabilizer, lubricant, the preparation method of the electromagnetic shielding composite materials with mechanical thermal conductivity PBT with excellent performance, good thermal conductivity and metallic luster surface visual effect, also has the function of electromagnetic wave shielding, and low cost, easy recycling, has very good practical application in electronic products.
【技术实现步骤摘要】
具有屏蔽作用的导热PBT复合材料及制备方法
本专利技术属于高分子材料
，涉及一种具有屏蔽作用的导热PBT复合材料及制备方法，该材料可广泛应用于电话、笔记本电脑等电子产品领域。
技术介绍
聚对苯二甲酸丁二醇酯（PBT）树脂是一种性能优良的热塑性工程塑料，它是半结晶材料，有非常好的化学稳定性、机械强度、电绝缘特性和热稳定性。这些材料在很广的环境条件下都有很好的稳定性。具有突出的电绝缘能力，耐热、成型性好，广泛应用于汽车、家用器具、仪器仪表、电器元件等领域。电磁屏蔽是电磁兼容技术的主要措施之一。即用金属屏蔽材料将电磁干扰源封闭起来，使其外部电磁场强度低于允许值的一种措施；或用金属屏蔽材料将电磁敏感电路封闭起来，使其内部电磁场强度低于允许值的一种措施。电磁屏蔽体:主要用来遏止高频电磁场的影响，使干扰场在屏蔽体内形成涡流并在屏蔽体与被保护空间的分界面上产生反射，从而大大削弱干扰场在被保护空间的场强值，达到了屏蔽效果。有时为了增强屏蔽效果，还可采用多层屏蔽体，其外层一般采用电导率高的材料，以加大反射作用，而其内层则采用磁导率高的材料，以加大涡流效应。常用的屏蔽材料，如铝...
【技术保护点】
一种具有屏蔽作用的导热PBT复合材料，其特征在于：该导热PBT复合材料由下述重量份数的原料构成聚对苯二甲酸丁二醇酯 50~75%；增韧剂 4~25%；偶联剂 0.1~1%；铝粉 10~40%；抗氧剂 ...
【技术特征摘要】
1.一种具有屏蔽作用的导热PBT复合材料，其特征在于：该导热PBT复合材料由下述重量份数的原料构成聚对苯二甲酸丁二醇酯50~75%；增韧剂4~25%；偶联剂0.1~1%；铝粉10~40%；抗氧剂0.1~0.2%；润滑剂0.2~0.8%。2.根据权利要求所述的具有屏蔽作用的导热PBT复合材料，其特征在于：所述聚对苯二甲酸丁二醇酯为中粘的线性聚对苯二甲酸丁二醇酯，熔融指数在10~15g/10min或24~32。3.根据权利要求1所述的具有屏蔽作用的导热PBT复合材料，其特征在于：所述铝粉目数为3000~5000。4.根据权利要求1所述的具有屏蔽作用的导热PBT复合材料，其特征在于：所述的增韧剂为在POE弹性体上接枝丙烯酸酯（AA）和缩水甘油脂（GMA）双官能团制得。5.根据权利要求1所述的具有屏蔽作用的导热PBT复合材料，其特征在于：所述的偶联剂为氨丙基三乙氧基硅烷。6.根据权利要求1所述的具有屏蔽作用的导热PBT复合材料，其特征在于：所述的抗氧化剂为受阻胺类抗氧剂和有机亚磷酸盐的复配物。7.根据权利要求1所...