The present invention discloses a new high strength anti ultraviolet woven tape production process. It includes the formulation and production process: 75%, 80% formula composed of polypropylene linear low density polyethylene 20% 25%, 7% 10%, 0.04 diatomite antioxidant 0.08%, anti UV agent, silane coupling agent 0.07 0.1% 0.05% 0.1%. The production process consists of: melting, extrusion, cooling water, touch wire, wire drawing and setting, including the procedures of rolling ingot. The invention has the advantages of simple formula, low cost, easy assembly, continuous production process, easy operation and control.
【技术实现步骤摘要】
一种新型高强抗紫外线塑编扁丝生产工艺
本专利技术涉及塑料编织应用领域,尤其是一种新型高强抗紫外线塑编扁丝生产工艺。
技术介绍
公知聚丙烯(pp)是一种半结晶的热塑性塑料,具有较高的耐冲击性以及机械性能强韧,抗多种有机溶剂和耐酸碱腐蚀等优点,缺点是低温下宜脆、宜老化、不耐磨。聚乙烯(PE)热塑性树脂,具有优良的耐低温性能和化学稳定性,尤其是线形低密度聚乙烯所具有的较高抗张强度,较好的抗穿刺性、抗撕裂性和能耐大多数酸碱的侵蚀,电绝缘性能优良,缺点是塑形差,不宜单独应用于塑编编织中。
技术实现思路
本专利技术是基于聚丙烯、聚乙烯材料特性,通过合理组配,提供一种新型高强抗紫外线塑编扁丝生产工艺,使生产出来的新型高强抗紫外线塑编扁丝具有优良特性,应用在塑编编织中不仅顺畅易编,而且生产出来的产品具有外观匀润、耐磨、抗拉、不易破损、循环利用率高等优点。本专利技术所述包括配方和生产工艺:配方由聚丙烯80%-75%、线性低密度聚乙烯20%-25%、硅藻土7%-10%、抗氧剂0.04-0.08%、抗紫外线剂0.07-0.1%、硅烷偶联剂0.05%-0.1%组成,生产工艺由:熔融、挤压出摸、水冷、分丝、拉丝、定型、卷锭等工序组成。本专利技术所述硅藻土需预处理,将硅藻土放入搅拌机中再倒入稀释后的硅烷偶联剂进行搅拌,待充分混合均匀分散后取出,即完成。本专利技术所述熔融、挤压出摸,按区段分为融料区170℃-180℃度、塑化区200℃-210℃度、混炼区205℃-215℃度、出摸保温区160℃-170℃度。本专利技术所述定型温度为85%℃-95%℃。本专利技术具有如下优点:1)按照新型高强 ...
【技术保护点】
一种新型高强抗紫外线塑编扁丝生产工艺, 其特征在于包括配方和生产工艺:配方由聚丙烯80%‑75%、线性低密度聚乙烯20%‑25%、 硅藻土7%‑10%、抗氧剂0.04‑0.08% 、抗紫外线剂0.07‑0.1%、硅烷偶联剂0.05%‑0.1%组成,生产工艺由:熔融、挤压出摸、水冷、分丝、拉丝、定型、卷锭等工序组成。
【技术特征摘要】
1.一种新型高强抗紫外线塑编扁丝生产工艺,其特征在于包括配方和生产工艺:配方由聚丙烯80%-75%、线性低密度聚乙烯20%-25%、硅藻土7%-10%、抗氧剂0.04-0.08%、抗紫外线剂0.07-0.1%、硅烷偶联剂0.05%-0.1%组成,生产工艺由:熔融、挤压出摸、水冷、分丝、拉丝、定型、卷锭等工序组成。2.根据权利要求1所述的一种新型高强抗紫外线塑编扁丝生产工艺,其特征在于所述硅藻土需预处理,将...