The present invention relates to the technical field of solar cells, especially the use of electrode paste for solar cell, the number of copies in accordance with the quality plan comprises the following components: 35 glass powder 50, tin bismuth alloy powder 40 60, adjacent benzene two formic acid two 12 octyl methyl cellulose 9 16 copies, 13 copies, poly glycol 8 15, two 10 tin oxide powder 15, polyoxyethylene polyoxypropylene glycerol ether 7 15. Using the above formula, the printing performance is improved greatly with the solar cell electrode paste conductive paste, reduce the sintering after the gate line collapsed, resistance reducing gate line; in addition, the non silver materials, reduce the production cost.
【技术实现步骤摘要】
太阳能电池用电极浆料
本专利技术涉及太阳能电池
,特别是一种太阳能电池用电极浆料。
技术介绍
晶体硅太阳能电池占据了光伏市场电池量的80%以上的份额,并且有望成为未来电力供应的主要支柱。降低太阳能电池的成本是光伏发电民用化的一个重要方向。目前商业的制作晶体硅太阳能电池背电极的方法是采用丝网印刷银导电浆料的方法,该工艺简单成熟,便于规模化生产。但是,银导电浆料成本相对较高。如何采用非银(或少银)材料制备电池的背面电极,是目前太阳能电池降低成本的一个重要方向。中国专利技术专利CN104752531A公开了一种太阳能电池用电极浆料,含有锡合金粉和助焊剂,所述助焊剂含有无机盐、增稠剂、有机溶剂和触变剂,其中,所述无机盐含有氟硼酸盐和/或卤化物,所述卤化物含有氟化物和氯化物。
技术实现思路
本专利技术需要解决的技术问题是提供一种太阳能电池用电极浆料。为解决上述的技术问题,本专利技术的太阳能电池用电极浆料,按照质量份数计包括以下组分:玻璃粉35-50份,锡铋合金粉40-60份,邻苯二甲酸二辛酯12-16份,甲基纤维素9-13份,聚乙二醇8-15份,二氧化锡粉末10-15份,聚氧丙烯聚氧乙烯甘油醚7-15份。进一步的,按照质量份数计包括以下组分:玻璃粉35份,锡铋合金粉40份,邻苯二甲酸二辛酯12份,甲基纤维素9份,聚乙二醇8份,二氧化锡粉末10份,聚氧丙烯聚氧乙烯甘油醚7份。进一步的,按照质量份数计包括以下组分:玻璃粉50份,锡铋合金粉60份,邻苯二甲酸二辛酯16份,甲基纤维素13份,聚乙二醇15份,二氧化锡粉末15份,聚氧丙烯聚氧乙烯甘油醚15份。进一步的,按照质 ...
【技术保护点】
一种太阳能电池用电极浆料,其特征在于,按照质量份数计包括以下组分:玻璃粉35‑50份,锡铋合金粉40‑60份,邻苯二甲酸二辛酯12‑16份,甲基纤维素9‑13份,聚乙二醇8‑15份,二氧化锡粉末10‑15份,聚氧丙烯聚氧乙烯甘油醚7‑15份。
【技术特征摘要】
1.一种太阳能电池用电极浆料,其特征在于,按照质量份数计包括以下组分:玻璃粉35-50份,锡铋合金粉40-60份,邻苯二甲酸二辛酯12-16份,甲基纤维素9-13份,聚乙二醇8-15份,二氧化锡粉末10-15份,聚氧丙烯聚氧乙烯甘油醚7-15份。2.按照权利要求1所述的太阳能电池用电极浆料,其特征在于,按照质量份数计包括以下组分:玻璃粉35份,锡铋合金粉40份,邻苯二甲酸二辛酯12份,甲基纤维素9份,聚乙二醇8份,二氧化锡粉末10份,聚氧丙烯聚氧乙烯甘油醚7份。3.按照权利要求1所述的太阳能电池用电极浆料,其特征在于,按照质量份数计包括以下组分:玻璃粉50份,锡铋...