The present invention discloses high silicon aluminum calcium reinforced fiber and its preparation method and aluminum calcium superplastic alloy base composite aluminum. According to the weight percentage, is composed of calcium oxide and 1% igneous rocks, 89% 98% 1 10% toner. On the basis of natural high silicon aluminum igneous rock ore, an amorphous high silicon aluminum calcium reinforced fiber is formed by introducing calcium oxide component. The amorphous calcium and high silicon aluminum fiber reinforced aluminum calcium superplastic Aluminum Alloy composite, reinforced silicon, aluminum and calcium group in the material, and the metal melt molecular fusion, so as to improve the binding strength of composite interface, improve the alloy based composite aluminum calcium super plastic strength.
【技术实现步骤摘要】
高硅铝钙增强纤维及其制备方法与铝钙超塑合金基复合铝
本专利技术涉及铝基复合材料制备领域，尤其涉及一种非晶高硅铝钙增强纤维及其制备方法，以及采用该纤维增强的铝钙超塑合金基复合铝。
技术介绍
铝材第一代是纯铝（1825年，丹麦奥斯特），第二代是合金铝（1903年，美国铝业公司），铝材第三代是陶瓷嵌合铝（1950s），第四代是非晶无机材料增强复合铝（2007，南京天淦新材料科技有限公司）。复合铝比钢更轻、更强、更多、更耐磨、更防腐，可以用来替代钢材，减少机动车船的能耗。在用于替代汽车/轮船的钢铁外壳时，复合铝延展性能应尽量和钢材靠近。由于复合铝增强材料，是一种高刚性的非晶无机材料。采用熔喷成形获得的基质材料为7050的航空复合铝，为了确保断裂延伸率落入4-5.5%的范围，其增强材料的添加量仅为3%左右。因此，现有技术还有待于改进，在提高复合铝增强材料添加量的同时，使得复合铝仍保有较高断裂延伸率。
技术实现思路
鉴于上述现有技术的不足，本专利技术的目的在于提供一种非晶高硅铝钙增强纤维及制备方法，并采用该纤维和高断裂延伸率的铝钙超塑合金复合。旨在提高复合界面亲和力（即拉伸强度）...
【技术保护点】
一种非晶高硅铝钙增强纤维，其特征在于，按重量百分比计，由89%‑98%的火成岩、1‑10%的氧化钙和1%的碳粉组成。
【技术特征摘要】
1.一种非晶高硅铝钙增强纤维，其特征在于，按重量百分比计，由89%-98%的火成岩、1-10%的氧化钙和1%的碳粉组成。2.根据权利要求1所述的非晶高硅铝钙增强纤维，其特征在于，按重量百分比计，由90%-95%的火成岩、4-9%的氧化钙和1%的碳粉组成。3.根据权利要求2所述的非晶高硅铝钙增强纤维，其特征在于，按重量百分比计，由90.1%的火成岩、8.9%的氧化钙和1%的碳粉组成。4.根据权利要求2所述的非晶高硅铝钙增强纤维，其特征在于，按重量百分比计，由94.3%的火成岩、4.7%的氧化钙和1%的碳粉组成。5.根据权利要求2所述的非晶高硅铝钙增强纤维，其特征在于，按重量百分比计，由93.74%的火成岩、5.26%的氧化钙和1%的碳粉组成。6.根据权利要求1所述的非晶高硅铝钙增强纤维，其特征在于，以火成岩为基准，所述火成岩所含氧化铁、氧化亚铁的总重量<3%，所述火成岩所含氧化硅、氧化铝的总重量>68%。7.一种如权利要求1~6任一所述的非晶高硅...
【专利技术属性】
技术研发人员：刘华武，戴洪明，孙瀚，
申请(专利权)人：深圳市正佳科建科技有限公司，
类型：发明
国别省市：广东,44
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。