The invention discloses a method for recovering precious metals before pretreatment from plasma furnace material enrichment, mainly relates to a plasma furnace from the failure of palladium enrichment material by smelting alumina catalyst in. Technical feature of the method is to add NaOH and NaNO3 to the enrichment of material good grinding, mixing in the furnace in melting the metal key Fe Pd Si P alloy was destroyed, the noble metal palladium generated insoluble in water is easily dissolved palladium compound sodium, high dissolved palladium the rate of. The invention has the advantages of low production cost, high dissolution rate of platinum group metals, effectively shortening the technological process and production cycle, and reducing the overstock of precious metal palladium.
【技术实现步骤摘要】
等离子炉富集料回收贵金属前的预处理方法
本专利技术涉及贵金属二次资源综合利用领域，尤其适合采用等离子炉从失效钯-氧化铝催化剂中熔炼得到的富集料回收贵金属前的预处理方法。
技术介绍
从失效钯-氧化铝基催化剂中回收贵金属钯的方法主要有湿法和火法。火法主要有铜捕集法和等离子炉熔炼-铁捕集法。等离子熔炼技术具有物料适应能力强、批次处理能力大、连续操作、贵金属回收率高、环境友好等优点，已被世界著名贵金属公司广泛采用。采用等离子熔炼技术对失效钯-氧化铝催化剂处理得到的贵金属钯富集料是一种Fe-Pd-Si-P合金，贵金属钯的含量为2-7％，铁、硅和磷会形成Fe3Si、Fe2Si、Fe5SiP、Fe3P等多种金属合金，此类合金极其惰性，具有很强的抗腐蚀性，用常用的HCl+Cl2或HCl+NaClO3，甚至王水都很难溶解，钯的溶解率较低。贵金属钯的分离提纯都是在盐酸体系下进行的，分离提纯钯前，必须对等离子炉钯富集料进行预处理，使钯富集料Fe-Pd-Si-P合金中的金属键断裂，同时使钯转换成更易被盐酸溶解的活化物。中国专利CN104073625A公开了一种等离子熔炼富集料回收贵金属前...
【技术保护点】
一种等离子炉富集料回收贵金属前的预处理方法，其特征在于：采用等离子炉对失效钯‑氧化铝催化剂熔炼得到的富集料为原料，磨粉后添加NaOH和NaNO3，混匀后在电炉中熔融，贵金属钯被硝酸钠氧化生成不溶于水易被酸溶解的钯酸钠(Na2PdO3)化合物，具体按如下步骤依次进行：(1)球磨：将预处理物料球磨至100‑200目；(2)配料：将磨细的物料与NaOH和NaNO3充分混匀；(3)熔融：将混好的物料装入不锈钢容器中，置于马弗炉内升温熔融；(4)溶解：将熔融物转入玻璃烧杯中，加入4‑6M盐酸，加热溶解，钯的溶解率大于97％，骤(2)中所述的物料与NaOH和NaNO3的比例为：物料︰N...
【技术特征摘要】
1.一种等离子炉富集料回收贵金属前的预处理方法，其特征在于：采用等离子炉对失效钯-氧化铝催化剂熔炼得到的富集料为原料，磨粉后添加NaOH和NaNO3，混匀后在电炉中熔融，贵金属钯被硝酸钠氧化生成不溶于水易被酸溶解的钯酸钠(Na2PdO3)化合物，具体按如下步骤依次进行：(1)球磨：将预处理物料球磨至100-200目；(2)配料：将磨细的物料与NaOH和NaNO3充分混匀；(3)熔融：将混好的物料装入不锈钢容器中，置于马弗炉内升温熔融；(4)溶解：将熔融物...
【专利技术属性】
技术研发人员：贺小塘，吴喜龙，赵雨，施秋杰，王欢，韩守礼，郭俊梅，李勇，汤永松，赵金成，王华，李子璇，李红梅，李佳莹，
申请(专利权)人：贵研资源易门有限公司，
类型：发明
国别省市：云南,53