一种用于改善马氏体时效不锈钢力学性能的热处理方法技术
A heat treatment method for improving the mechanical properties of Maraging Stainless Steel
The present invention discloses a heat treatment method for improving the mechanical properties of Maraging Stainless steel. The steps are as follows: 1) selection of maraging stainless steel as the material heat treatment; 2) the solution of steel pickling and cleaning and drying cleaning liquid; 3) on dried steel for cold rolling; 4) after the treatment of cold rolling steel aging treatment right; 5) after treatment of steel cleaning liquid for cleaning and drying treatment. The heat treatment process for improving the mechanical properties of maraging stainless steel provided by the invention is simple and easy, and the equipment and drugs involved are more common and easy to obtain. Based on the normal heat treatment, the method can effectively select the corresponding aging treatment parameters, and reduce the possibility of brittle fracture in the process of using the needle.
【技术实现步骤摘要】
一种用于改善马氏体时效不锈钢力学性能的热处理方法
本专利技术涉及金属材料的热处理工艺，尤其涉及一种用于改善马氏体时效不锈钢力学性能的热处理方法。
技术介绍
医用缝合针在外科手术中作为一种不可或缺的器材，其对强度、硬度和韧性都有着极高的要求。现阶段马氏体不锈钢，其中最典型的是3Cr13，大量应用于缝合针的制造中。但是，该材料有着一个致命的缺点，即脆性大，因此临床使用过程中关于缝合针断裂的事故屡见不鲜，给医生带来了极大的不方便并给患者带来了痛苦。为有效解决缝合针使用过程中发生断裂的问题，马氏体时效不锈钢被应用于该领域，因为其在超高强度的同时拥有良好的韧性。而马氏体时效不锈钢超高强度和良好任性主要归因于其在时效过程中，马氏体时效不锈钢内部组织发生变化，即析出了大量的第二相。因此，这些析出相的状态对马氏体时效不锈钢的性能尤为重要，这也决定了其在缝合针领域应用的优劣程度。现阶段对于马氏体时效不锈钢时效温度的选择，国内普遍使用的是350-600℃。虽然马氏体时效不锈钢在该温度区间时效一定时间后相较于固溶态在硬度方面有较大提高，但是在有些温度区间时效时易发生脆性断裂，从而导致事...
【技术保护点】
一种用于改善马氏体时效不锈钢力学性能的热处理方法，它的步骤如下：1)选择马氏体时效不锈钢作为热处理材料；2)将固溶后的钢材进行酸洗并使用清洗液进行清洗及干燥处理；3)对干燥处理后的钢材进行冷轧处理；4)将冷轧处理后的钢材进行合适的时效处理；5)将处理后的钢材用清洗液进行清洗及干燥处理。
【技术特征摘要】
1.一种用于改善马氏体时效不锈钢力学性能的热处理方法，它的步骤如下：1)选择马氏体时效不锈钢作为热处理材料；2)将固溶后的钢材进行酸洗并使用清洗液进行清洗及干燥处理；3)对干燥处理后的钢材进行冷轧处理；4)将冷轧处理后的钢材进行合适的时效处理；5)将处理后的钢材用清洗液进行清洗及干燥处理。2.根据权利要求1所述的热处理方法，其特征在于：所述的酸洗的腐蚀液的体积比组成为HF:HNO3:H2O＝1：3：10，处理时间为30min。3.根据权利要...