以甲胺铅溴钙钛矿量子点制备钙钛矿量子点纳米棒的方法技术

本发明专利技术公开了一种以甲胺铅溴钙钛矿量子点制备钙钛矿量子点纳米棒的方法，步骤一、将载玻片进行清洗，先倒入食人鱼溶液(浓硫酸和30％过氧化氢按7:3)并煮沸30分钟，再依次倒入乙醇溶液和去离子水溶液，各超声清洗15‑30分钟，取出用氮气吹干；步骤二、将甲胺铅溴钙钛矿量子点的二甲基甲酰胺DMF溶液溶于甲苯中配置成1ⅹ10

Preparation of perovskite quantum dots nanorods with methylamine, lead and bromine perovskite quantum dots

The invention discloses a method for preparing perovskite nanorods using quantum dot quantum dot perovskite lead methylamine bromide, a step, the slides were washed first into piranha solution (sulfuric acid and hydrogen peroxide by 30% 7:3) and boil for 30 minutes, then turn into the ethanol solution and deionized water solution, the ultrasonic cleaning 15 took 30 minutes, dried by nitrogen; step two, two DMF solution of methyl bromide DMF lead perovskite QDs dissolved in toluene in configuration into 1 \10

【技术实现步骤摘要】
以甲胺铅溴钙钛矿量子点制备钙钛矿量子点纳米棒的方法
本专利技术涉及一种以甲胺铅溴钙钛矿量子点为原料组装钙钛矿量子点纳米棒的技术,属于量子点纳米棒制备

技术介绍
量子点新型发光材料具有吸收范围宽、发光带窄、光稳定性强等优点，且可以通过控制其尺寸及组成可获得发光颜色覆盖整个可见光波段的各种单色光，因此量子点可以作为一种新型的发光材料用于LED领域。而纳米棒结构因具有独特的物理、化学性能以及在光、电、催化和存储等领域具有重要潜在应用价值而倍受人们的关注。但是目前制备甲胺铅溴钙钛矿量子点纳米棒的方法是将乙酸铅的饱和甲醇溶液涂布到涂覆有PEDOT:PSS的ITO玻璃基底上，再将基底放置到CH3NH3Br溶液中。其整个制备过程需要几十个小时而且需要旋涂、烘烤、退火等步骤，导致制备周期长和生产工艺繁杂。因此，利用甲胺铅溴钙钛矿量子点的自组装特性来制备甲胺铅溴钙钛矿量子点纳米棒并将其应用在固态照明领域具有重要的意义，这将为固态照明领域提供一种可加工性好、可大批量生产、成本较低的可用于搭建新型LED器件的发光层。
技术实现思路
技术问题：本专利技术的目的是提供一种以甲胺铅溴钙钛矿量子点为原料制备本文档来自技高网...

【技术保护点】
一种以甲胺铅溴钙钛矿量子点制备钙钛矿量子点纳米棒的方法，其特征在于，该方法包括如下步骤：步骤一、将载玻片进行清洗，先倒入食人鱼溶液并煮沸30分钟，再依次倒入乙醇溶液和去离子水溶液，各超声清洗15‑30分钟，取出用氮气吹干；步骤二、将甲胺铅溴钙钛矿量子点的二甲基甲酰胺DMF溶液溶于甲苯中配置成1ⅹ10