一种新型白色长余辉发光材料及其制备方法技术
Novel white long afterglow luminescent material and preparation method thereof
The invention discloses a novel white long afterglow luminescent material, wherein the molecular formula of the material is Zn2GeO4, and the main phase structure belongs to the rhombohedral system. The invention adopts the method of high temperature solid phase synthesis, mixes ZnO and GeO2 by grinding, and then cools and gets white long afterglow luminescent material. After being excited by an ultraviolet lamp of 254nm, the Zn2GeO4 of the invention has a band afterglow spectrum spanning 400nm to 700nm, and the white light is emitted by the naked eye, and the white long afterglow is still emitted after the light source is removed. The material has good color purity and excellent afterglow performance, and the synthetic method is simple and easy to realize.
【技术实现步骤摘要】
一种新型白色长余辉发光材料及其制备方法
本专利技术涉及长余辉材料
更具体地，涉及一种新型白色长余辉发光材料及其制备方法。
技术介绍
长余辉发光材料属于光致发光材料，它在紫外光、可见光的激发下储存能量，激发停止后，以可见光的形式缓慢释放能量，是一种节能材料，广泛应用于应急照明、交通标志、安全指示、装饰工艺等。迄今为止，研究比较成熟的长余辉发光材料覆盖了从蓝色到红色的大部分区域，然而最适宜于用作照明光源的白色长余辉材料距离使用要求尚有较大差距。白色长余辉材料的研究，最初人们是按照合成白色光的原理，将两种或多种发不同颜色光的材料进行复合，使两种或多种光叠加对外呈现出白色。在2005年，刘应亮、刘波等人报道了CdSiO3:Dy3+、CaAl2O4∶Dy3+的白色长余辉现象。2006年，KuangJ等人制备出白色长余辉发光材料SrSiO3:Dy3+，并将其发光性质与刘应亮的研究进行了对比。2008年，陈永虎等人采用高温固相法制备了白色长余辉发光材料CaxMgSi2O5+x：Dy3+(x＝1，2，3)，并对其进行了研究分析。不难发现，以上几种白色长余辉发光材料均为单掺...
【技术保护点】
一种新型白色长余辉发光材料，其特征在于，所述材料的分子式为Zn2GeO4，主相结构属于菱方晶系。
【技术特征摘要】
1.一种新型白色长余辉发光材料，其特征在于，所述材料的分子式为Zn2GeO4，主相结构属于菱方晶系。2.根据权利要求1所述的一种新型白色长余辉发光材料，其特征在于，所述白色长余辉发光材料为玻璃陶瓷状。3.如权利要求1～2任一所述的一种新型白色长余辉发光材料的制备方法，其特征在于，包括如下步骤：将ZnO与GeO2研磨混匀后煅烧，冷却后得到白色长余辉发光材料。4.根据权利要求3所述的一种新型白色长余辉发光材料的制备方法，其特征在于，所述ZnO与GeO2的物质的量之比为1:0.5～1。5.根据权利要求3所述的一种新型白色长余辉发光材料的制备方法，其特征在于，所述ZnO与GeO2的物质的量之比为1:0.75～1。6.根据权利要求3所述的一种新型白色长余辉发光材料的制备方法，其特征在于，所述煅烧方式为升温至120...
【专利技术属性】
技术研发人员：段晓霞，袁满，衣立新，张希清，徐征，
申请(专利权)人：北京交通大学，
类型：发明
国别省市：北京,11