污泥制砖技术制造技术

一种利用制砖方式对剩余污泥进行彻底处置的技术。它是将含水为60％的湿污泥利用砖厂余热进行干化，以总重量8％‑10％的比例，同黏土、煤矸石一起作为制砖原料。干化后的污泥进入粉碎车间，进行粉碎，后与黏土在陈化车间堆积，进行陈化。在供土机中，黏土、煤矸石、污泥等制砖原料混合均匀，后经强力搅拌机搅拌，以增加粘结度，再进制砖机，切坯机，制成砖坯，制得烧结砖。主要适用于对城市污水处理厂产生的剩余污泥进行彻底处置。

Sludge making brick technology

A technique for thoroughly disposing excess sludge by brick making method. It is the water for wet sludge using waste heat to dry brick 60%, with a total weight of 8% the proportion of 10%, the same as with clay, coal gangue brick making raw materials. After drying, the sludge enters the crushing workshop and is crushed, and then it is piled up with the clay in the aging workshop. In the soil for machine, clay, coal gangue brick, sludge and other raw materials are mixed evenly, after strong stirring, in order to increase the bonding of the band again brick machine, cutting machine, made of brick, brick prepared. It is mainly applicable to the disposal of excess sludge produced by municipal wastewater treatment plants.

【技术实现步骤摘要】
污泥制砖技术所属
：本专利技术涉及一种利用制砖方式对剩余污泥进行彻底处置的技术。尤其是中小城市污水处理厂剩余污泥的处置。
技术介绍
：目前，我国85％的污泥以填埋处理作为最终的处置方式。随着国家对污泥处置工作的逐渐重视，各地在污泥处置方面也有诸如：堆肥、土地利用、建材利用等方式的探讨和研究。但采用以上方式，不同程度的存在成本高、“二次污染”严重、浪费消耗资源以及产品销路等方面的问题。
技术实现思路
：为了彻底解决污泥处置中“二次污染”、占用土地、资源浪费等诸多不足，本专利技术提供一种污泥制砖技术，该技术不仅能彻底处置剩余污泥，而且能充分利用污泥中的热值，达到废弃物“减量化”、“资源化”、“再利用”。附图说明：图1是将污泥、煤矸石、粘土按一定比例配比制的的烧结砖图样。具体实施方式：本专利技术解决其技术问题所采用的技术方案是：将含水率为60％的湿污泥运到砖厂后，先送往干化车间，利用厂内余热进行干化，干化后的污泥以总重量8％-10％的比例，同黏土、煤矸石一起作为制砖原料。干化后的污泥进入粉碎车间，进行粉碎，后与黏土在陈化车间堆积，进行陈化，在供土机中与黏土、煤矸石、污泥等制砖原料混合均匀，后经本文档来自技高网...

【技术保护点】
一种剩余污泥处置技术。其特征是：将剩余污泥作为制砖原料，掺和到其他制砖原料中，进行制砖。

【技术特征摘要】
1.一种剩余污泥处置技术。其特征是：将剩余污泥作为制砖原料，掺和到其他制砖原料中，进行制砖。2.根据权利要求1所述的“污泥制砖”技术，其特征是：将剩余污泥以不大于10％的比例，掺配到其它制砖原料中，制得烧结砖。3.根据权利要...

【专利技术属性】
技术研发人员：李心海，王丽萍，李子文，周润华，
申请(专利权)人：李心海，王丽萍，李子文，
类型：发明
国别省市：山西,14