一种电动机定子绕组的环氧树脂浇注工艺制造技术
Epoxy resin pouring process for motor stator winding
The present invention discloses epoxy resin casting process of stator winding of a motor, which comprises the following steps: (1) of epoxy resin and curing agent are mixed according to the ratio of heating after pouring liquid; (2) the pouring liquid poured into the stator winding, pouring liquid immersion meditation winding enameled wire and the gap between the enameled wire and a stator core; (3) after the casting solidification. The invention adopts epoxy resin casting insulation to solve the problem of engine stator winding, stator and mould is formed with the casting space, casting liquid to the casting space, casting in place after curing, enter the space and motor stator epoxy resin as a whole, forming a protective shell, improve the protection ability.
【技术实现步骤摘要】
一种电动机定子绕组的环氧树脂浇注工艺
本专利技术涉及电动机定子绕组的的防护
，具体涉及一种电动机定子绕组的环氧树脂浇注工艺。
技术介绍
电动机的定子是重要组成部分，定子内的定子绕组通过电流时，定子产生旋转磁场，为电机转动提供动力。定子绕组的导热性能及绝缘防护尤为重要，其直接影响电能损耗及电机寿命，目前常用的绝缘方式是通过沉浸绝缘漆，来提高定子的绝缘及散热。例如，公开号为CN101707406A的中国专利技术专利申请文献公开了一种耐高水压潜水电动机，它具有壳体、定子和转子、端盖、接线盒，定子包括定子铁芯和定子绕组，定子绕组引出线与引接电缆线焊接连接，定子绕组内部滴注有滴浸绝缘漆，外部整体包敷有滴浸绝缘漆膜，定子绕组引出线及其与引接电缆线的连接部位缠绕包裹有多层柔性绝缘带，该绝缘带外部套装有橡胶套管及依次缠绕包裹在橡胶套管上的柔性绝缘带和玻璃布带。该电动机通过对定子绕组及引出线和引接电缆线的滴浸绝缘和绝缘带的包扎等封装工艺，能够保证电动机在210℃高温及20MPa高压导电液体介质中安全可靠的运行。但沉浸工艺的缺点有以下几点：1、漆包线与铁芯间的较大缝隙无法填充，...
【技术保护点】
一种电动机的定子绕组的环氧树脂浇注工艺，其特征在于，包括如下步骤：(1)将环氧树脂与固化剂分别加热后按配比混合成浇注液；(2)将所得浇注液浇注至所述定子绕组中，浇注液浸入定子绕组的漆包线之间以及漆包线与定子铁芯的缝隙中；(3)浇注完成后进行固化。
【技术特征摘要】
1.一种电动机的定子绕组的环氧树脂浇注工艺，其特征在于，包括如下步骤：(1)将环氧树脂与固化剂分别加热后按配比混合成浇注液；(2)将所得浇注液浇注至所述定子绕组中，浇注液浸入定子绕组的漆包线之间以及漆包线与定子铁芯的缝隙中；(3)浇注完成后进行固化。2.根据权利要求1所述环氧树脂浇注工艺，其特征在于，环氧树脂和固化剂的加热温度均为40～60℃，加热时间均为10-15分钟。3.根据权利要求1所述环氧树脂浇注工艺，其特征在于，环氧树脂与固化剂按质量比4～5:1进行配比。4.根据权利要求1所述环氧树脂浇注工艺，其特征在于，步骤(2)中采用多次浇注方式进行浇注且在室温下进行。5.根据权利要求4所述环氧树脂浇注工艺，其特征在于，浇注液分三次完成浇注，第一次的浇注量为浇注总量的40～50％，第二次浇注的浇注量为浇注总量的30～40％，第三次完成剩余部分的浇注。6.根据权利要求5所述环氧树脂浇注工艺...
【专利技术属性】
技术研发人员：侯金刚，罗伟朝，
申请(专利权)人：浙江西子富沃德电机有限公司，
类型：发明
国别省市：浙江,33
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。