The invention discloses a road repair mortar, the road repair mortar consists of the following materials by weight percentage: 300 compounded cement 350 weight dispersible latex powder 45, 60 weight, 1 to 2 parts by weight of cellulose ether, defoaming agent 1 2 parts by weight of silica powder 30, 40 weight, early strength agent 1 3 weight portions, water reducing agent 1 3 weight portions, 70 to 120 margin quartz sand; wherein the cellulose ether is 35 thousand 50 thousand viscosity of carboxymethyl hydroxypropyl cellulose ether; the early strength agent for calcium formate purity greater than 97%. The invention has good workability, adhesive property, permeability resistance, spalling resistance, freeze-thaw resistance, carbonation resistance, cracking resistance, rust and other properties, and can repair the road in a relatively short period of time, to ensure the smooth road traffic.
【技术实现步骤摘要】
一种道路修补砂浆
本专利技术涉及建筑砂浆领域，具体涉及一种道路修补砂浆。
技术介绍
交通的发达大大提高了经济发展的速度，但是长时间高强度的使用公路，会造成路面不同程度的损坏，修补道路就是必要的工作，在修补道路上大量的应用到道路修补砂浆。修补砂浆是一种既具有高分子材料的粘接性，又具有无机材料耐久性的新型混凝土材料。其具有抗压强度高，固化迅速，粘接性能好等特点，且具有良好的保水性能和抗裂性、高耐碱性、耐紫外线等性能，可使施工步骤变得简单、方便，耐久性与混凝土同步，缩短工期，可确保经济性。
技术实现思路
为解决现有修补砂浆技术的不足，本专利技术提供一种道路高强度，快速硬化的修补砂浆。一种道路修补砂浆，其特征在于，其特征在于，该道路修补砂浆由以下材料按重量百分比配制而成：水泥300-350重量份，可分散性乳胶粉45-60重量份，纤维素醚1-2重量份，消泡剂1-2重量份，硅微粉30-40重量份，早强剂1-3重量份，减水剂1-3重量份，余量为70-120目的石英砂；其中所述的纤维素醚为3.5万-5万粘度的甲基羟丙基纤维素醚；所述的早强剂为纯度大于97%的甲酸钙。作为优选方案之一，...
【技术保护点】
一种道路修补砂浆，其特征在于，该道路修补砂浆由以下材料按重量百分比配制而成：水泥300‑350重量份，可分散性乳胶粉45‑60重量份，纤维素醚1‑2重量份，消泡剂1‑2重量份，硅微粉30‑40重量份，早强剂1‑3重量份，减水剂1‑3重量份，余量为70‑120目的石英砂；其中所述的纤维素醚为3.5万‑5万粘度的甲基羟丙基纤维素醚；所述的早强剂为纯度大于97%的甲酸钙。
【技术特征摘要】
1.一种道路修补砂浆，其特征在于，该道路修补砂浆由以下材料按重量百分比配制而成：水泥300-350重量份，可分散性乳胶粉45-60重量份，纤维素醚1-2重量份，消泡剂1-2重量份，硅微粉30-40重量份，早强剂1-3重量份，减水剂1-...