The present invention relates to a non metallic adsorbent for adsorptive desulfurization, in particular a boron deficient boron nitride nanosheets and its preparation method and application in adsorbing aromatic sulfides in fuel oil. The boric acid and nitrogen source were dissolved into ultrapure water, and then the common reaction source was added. The solution was agitated at 80~90 degrees. (2) the solution after evaporation, the solid in the tube furnace in nitrogen or ammonia atmosphere under 700 to 1000 DEG 5h by calcination, boron deficient boron nitride; part due to lack of boron atoms, resulting in boron nitride chemical hardness decreased, can form a good interaction with soft base two thiophene dibenzothiophene, thereby removing fuel in two benzothiophene.
【技术实现步骤摘要】
一种硼缺陷氮化硼纳米片及其制备方法和用途
本专利技术涉及吸附脱硫的非金属吸附剂，特指一种硼缺陷氮化硼纳米片及其制备方法和在吸附降低燃油中芳香硫化物的用途。
技术介绍
随着世界经济的发展，清洁燃料的开发越来越迫切。到目前为止，化石燃料仍是世界上的主要能源之一。然而，燃料中普遍存在的硫化合物燃烧后会释放SOx气体。这些气体不仅会导致酸雨，而且还会对人体造成伤害。因此，实现高效清洁燃料变得越来越重要。由于温和的操作条件和高选择性，吸附脱硫(ADS)受到越来越多的关注。最近，层状六方氮化硼(BN)已经被广泛的研究兴趣。在我们以前的报告中，BN材料已被证明能够用作吸附脱硫的非金属吸附剂(GreenChem.,2015,17,1647-1656)。尽管BN材料展现出一定的吸附脱硫能力，但其性能仍未达到工业应用潜力的要求。据以前的报道，软硬酸碱度(HSAB)理论在对ADS的作用中起着非常重要的作用(EnergyFuels,2008,22,3858-3863)。众所周知，软酸易与软碱反应，硬酸易发生与硬碱相互作用。由于硼原子存在空轨道，电子缺陷特征使其具有一定的吸电子能力，因此B...
【技术保护点】
一种硼缺陷氮化硼纳米片，其特征在于，采用如下方法制备：(1)将硼酸和氮源溶解到超纯水中，然后加入共反应源，上述溶液在80～90℃下搅拌蒸发；(2)待溶液全部蒸发完后，所得固体放入管式炉中在氮气或氨气的气氛下700～1000℃煅烧5h，得到硼缺陷氮化硼纳米片。
【技术特征摘要】
1.一种硼缺陷氮化硼纳米片，其特征在于，采用如下方法制备：(1)将硼酸和氮源溶解到超纯水中，然后加入共反应源，上述溶液在80～90℃下搅拌蒸发；(2)待溶液全部蒸发完后，所得固体放入管式炉中在氮气或氨气的气氛下700～1000℃煅烧5h，得到硼缺陷氮化硼纳米片。2.如权利要求1所述的一种硼缺陷氮化硼纳米片，其特征在于，所述的氮源是二氰二胺；所述硼酸和氮源的摩尔比是1:6～1:12。3.如权利要求2所述的一种硼缺陷氮化硼纳米片，其特征在于，所述硼...
【专利技术属性】
技术研发人员：熊君，罗静，杨磊，朱文帅，李华明，