一种ASA与PVC复合装饰材料及其制备方法技术
Composite decorative material of ASA and PVC and preparation method thereof
The invention discloses a composite decorative material of ASA and PVC and a preparation method thereof. The composite decorative material comprises a PVC layer and a ASA layer adhering to the upper surface of the PVC layer. The preparation methods of ASA and PVC composite decorative materials, including preheating steps, bonding steps, insulation steps, finalize the steps, winding steps. The ASA fit to form a composite material in PVC, high temperature resistance, good color stability, UV stability, weather resistance characteristics, especially suitable for outdoor use, use of color high decoration materials. The preparation method is simple, the production efficiency is high, the process condition is mild, and it can be produced on a large scale.
【技术实现步骤摘要】
一种ASA与PVC复合装饰材料及其制备方法
本专利技术涉及一种家居装饰材料技术，尤其涉及一种ASA与PVC复合装饰材料及其制备方法。
技术介绍
PVC为无定形结构的白色粉末，支化度较小。工业生产的PVC分子量一般在5万-12万范围内，具有较大的多分散性，分子量随聚合温度的降低而增加；无固定熔点，80-85℃开始软化，130℃变为粘弹态，160-180℃开始转变为粘流态；有较好的机械性能，抗张强度60MPa左右，冲击强度5-10kJ/m2；有优异的介电性能。PVC也正以其良好的性能、简单的工艺以及其他诸多优点渐渐赢得了人们的欢心，已被越来越多的人接受和认可，广泛应用在家居装饰材料中。但PVC装饰材料对光和热的稳定性差，在100℃以上或经长时间阳光曝晒，就会分解而产生氯化氢，并进一步自动催化分解，引起变色，物理机械性能也迅速下降。因此，对于户外使用的PVC装饰材料，经过日晒雨淋的时间验证，这些PVC装饰材料耐候性差，使用一年左右就会出现褪色、变色等现象。因此，针对户外使用、而且对颜色要求较高的装饰材料，现有的PVC装饰材料无法满足其使用要求的。
技术实现思路
为了克服现有...
【技术保护点】
一种ASA与PVC复合装饰材料，其特征在于，包括PVC层和贴合在PVC层上表面的ASA层。
【技术特征摘要】
1.一种ASA与PVC复合装饰材料，其特征在于，包括PVC层和贴合在PVC层上表面的ASA层。2.如权利要求1所述的ASA与PVC复合装饰材料，其特征在于，所述PVC层的厚度为0.05-6mm，所述ASA层的厚度为0.05-0.5mm。3.如权利要求1所述的ASA与PVC复合装饰材料，其特征在于，所述PVC层根据厚度的不同分为膜材和片材，其中PVC膜材厚度为0.05-0.5mm，PVC片材厚度为2.7-6mm。4.一种ASA与PVC复合装饰材料的制备方法，其特征在于包括，预热的步骤：卷有ASA的ASA卷材在第一导入辊筒的转动下带动其移动；卷有PVC的PVC卷材经过第二导入辊筒的转动下带动其移动，ASA与PVC移动时，在110-150℃下进行预热；贴合的步骤：所述ASA与PVC在热贴辊上进行热贴合，所述热贴合温度为150-160℃；保温的步骤：经热贴后的复合材料依次绕设在保温辊上进行保温处理，所述保温处理的温度为170-180℃；定型的步骤：经保温的复合材料依次绕设在冷却...