一种法兰表面打磨方法技术

本发明专利技术公开了一种法兰表面打磨方法，包括如下步骤：（1）浸泡：将法兰放在特制溶液中浸泡35‑45分钟；（2）粗磨：取出浸泡后的法兰并用棉布擦干，然后使用100#的干磨砂纸进行打磨；（3）细磨：用水冲洗掉附着在法兰表面的磨屑，然后将法兰擦干，使用400#的干磨纸对法兰进行打磨。本发明专利技术通过浸泡、粗磨、细磨、精磨及干燥处理等步骤的合理设置，并且在每次打磨前都对法兰进行冲洗，使得打磨后的法兰表面磨痕少，表面较光滑、平整。

A flange surface grinding method

The invention discloses a flange surface polishing method, which comprises the following steps: (1) immersion: flange soak in special solution for 35 45 minutes; (2) coarse grinding: remove the flange after soaking with dry cloth, and then use 100# dry sanding paper grinding; (3) fine grinding water wash away debris attached to the flange surface, and then dry the flange, dry grinding paper on flange grinding using 400#. The present invention by soaking, coarse grinding, fine grinding, fine grinding and drying a reasonable set of steps, and at each of the flange to wash before grinding, the flange surface after grinding grinding, surface is smooth and flat.

【技术实现步骤摘要】
一种法兰表面打磨方法
本专利技术属于法兰处理
，尤其是涉及一种法兰表面打磨方法。
技术介绍
法兰在工业生产中使用十分广泛，两个管道、管件或器材可以通过两个法兰固定连接在一起，连接时先各自固定在一个法兰盘上，然后在两个法兰盘之间加上法兰垫，最后用螺栓将两个法兰紧固连接在一起就实现了两个物体之间的固连，另外法兰连接不仅使用方便，而且还能够承受较大的压力。然而目前法兰表面的打磨工序还不够成熟，在打磨时容易在法兰表面留下较多的磨痕。
技术实现思路
本专利技术为了克服现有技术的不足，提供一种打磨后工件表面磨痕少的法兰表面打磨方法。为了实现上述目的，本专利技术采用以下技术方案：一种法兰表面打磨方法，包括如下步骤：(1)浸泡：将法兰放在特制溶液中浸泡35-45分钟；(2)粗磨：取出浸泡后的法兰并用棉布擦干，然后使用100#的干磨砂纸进行打磨；(3)细磨：用水冲洗掉附着在法兰表面的磨屑，然后将法兰擦干，使用400#的干磨纸对法兰进行打磨；(4)精磨：用水冲洗掉附着在细磨后法兰表面的打磨屑，然后将法兰擦干，使用800#的水磨纸对法兰进行打磨，打磨至法兰表面平整、光滑为止；(5)干燥处理：将经精磨后的本文档来自技高网...

【技术保护点】
一种法兰表面打磨方法，其特征在于：包括如下步骤：（1）浸泡：将法兰放在特制溶液中浸泡35‑45分钟；（2）粗磨：取出浸泡后的法兰并用棉布擦干，然后使用100#的干磨砂纸进行打磨；（3）细磨：用水冲洗掉附着在法兰表面的磨屑，然后将法兰擦干，使用400#的干磨纸对法兰进行打磨；（4）精磨：用水冲洗掉附着在细磨后法兰表面的打磨屑，然后将法兰擦干，使用800#的水磨纸对法兰进行打磨，打磨至法兰表面平整、光滑为止;（5）干燥处理：将经精磨后的法兰再次用水冲洗一遍，然后直接用吹风机吹干。

【技术特征摘要】
1.一种法兰表面打磨方法，其特征在于：包括如下步骤：（1）浸泡：将法兰放在特制溶液中浸泡35-45分钟；（2）粗磨：取出浸泡后的法兰并用棉布擦干，然后使用100#的干磨砂纸进行打磨；（3）细磨：用水冲洗掉附着在法兰表面的磨屑，然后将法兰擦干，使用400#的干磨纸对法兰进行打磨；（4）精磨：用水冲洗掉附着在细磨后法兰表面的打...

【专利技术属性】
技术研发人员：顾青龙，
申请(专利权)人：安吉圆磨机械科技有限公司，
类型：发明
国别省市：浙江,33