一种镀镍‑锌复合镀层的钢/铝钎焊方法技术
A nickel zinc composite coating of steel / aluminum brazing method
The invention provides a steel base metal nickel / zinc composite coating of steel / aluminum brazing method, which belongs to the field of dissimilar material joints, and is characterized in that the steel welding surface forming electroplating thickness of 0.1 M ~ 300 m nickel layer; then in steel with nickel plating welding surface on the formation of the plating thickness is 0.1 M ~ 300 m galvanized layer, finally welding. In the welding process, the nickel plating layer to suppress the diffusion of steel / aluminum elements, the reaction of a relief, to improve the mechanical properties of the joints by improving the metallurgical reaction; in addition, the outer layer of zinc melted during welding and brazing fusion, the solder spread on the steel base material has been greatly improved, to achieve fluxless connection. High quality joints are obtained.
【技术实现步骤摘要】
一种镀镍-锌复合镀层的钢/铝钎焊方法
本专利技术涉及一种镀镍-锌复合镀层的钢/铝钎焊方法，属于异种材料连接领域。
技术介绍
近年来，能源危机与环境问题越来越严重，在保证安全性能的前提下，轻量化已经成为一种必然趋势。而铝/钢复合结构具有质量轻、强度高等优点，在航空航天、船舶、汽车制造等领域正日益受到广泛的关注，显示出良好的应用前景。然而，钢/铝异种金属由于热物理化学性能的差异，且在焊接过程中极易形成脆性金属间化合物。采用钎焊是抑制钢/铝异种金属焊接脆性金属间化合物形成的有效方法，但是不能完全避免。而且液态铝在固态钢表面的润湿铺展性较差，采用钎焊的方法时必须使用钎剂或钢表面镀锌。传统镀锌钢虽然能够提高耐腐蚀性并提高钢/铝的可焊性，但对于导致焊接接头强度不足的金属间化合物层的问题收效甚微。因此，在改善液态铝对固态钢表面的润湿铺展性的基础上，改善钢/铝冶金反应和是钢/铝异种金属焊接亟待解决的问题。本专利技术提出一种新的钢母材镀镍-锌复合镀层的钎焊方法，同时实现镀锌层促进液态铝的润湿铺展与镀镍层抑制/改性脆性金属间化合物双重功能。
技术实现思路
本专利技术所要解决的技术问题在于...
【技术保护点】
一种镀镍‑锌复合镀层的钢/铝钎焊方法，其特征在于：具体步骤如下：A.在钢母材的焊接面上电镀形成镀镍层，其厚度为0.1μm～300μm；B.在带有镍镀层的钢母材的焊接面上电镀形成镀锌层其厚度为0.1μm～300μm；C.焊接。
【技术特征摘要】
1.一种镀镍-锌复合镀层的钢/铝钎焊方法，其特征在于：具体步骤如下：A.在钢母材的焊接面上电镀形成镀镍层，其厚度为0.1μm～300μm；B.在带有镍镀层的钢母材的焊接面上电镀形成镀锌层其厚度为0.1μm～300μm；C.焊接。2.根据权利要求1所述的一种镀镍-锌复合镀层的...
【专利技术属性】
技术研发人员：陈树海，李岩，黄继华，杨健，
申请(专利权)人：北京科技大学，
类型：发明
国别省市：北京,11