长期水性防锈剂及其制备方法技术

本发明专利技术公开一种长期水性防锈剂，包括以下质量分数的原料制备：三乙醇胺15‑17份、硼酸钠2‑3份、植酸1‑2份、树脂2‑3份、叔丁基苯甲酸0.1‑0.2份、甲基苯并三氮唑1‑2份、表面活性剂0.5‑1份、去离子水71.8‑78.4份。本发明专利技术还公开一种制备上述长期水性防锈剂的方法。本发明专利技术具有不会影响被防锈材料表面金属光泽，使用方便、易去除，防锈期长，可达一个月以上的优点。

Long term water based rust inhibitor and its preparation method

The invention discloses a long-term waterborne antirust agent, raw material preparation method includes the following content: 15 triethanolamine 17, sodium borate 2 3 copies, 2 copies, 1 phytic acid resin 2 3, tert butyl benzoic acid 0.1 0.2, methyl benzene and three triazole 1 2 0.5, surfactant 1, deionized water 71.8 78.4. The invention also discloses a method for preparing the above long-term water-based antirust agent. The invention has the advantages of no influence on the metal luster of the surface of the antirust material, convenient use, easy removal, long rust prevention period, and can reach more than one month.

【技术实现步骤摘要】
长期水性防锈剂及其制备方法
本专利技术涉及防锈剂
，尤其涉及长期水性防锈剂及其制备方法。
技术介绍
随着机械加工领域的扩大，中途运输防锈和工序间防锈成了热门话题。选择好的防锈剂能够节约成本，降低能耗，减少浪费，并减轻对操作者的危害。目前，国内市场的水基防锈剂性能参差不齐，其主要问题有防锈时间短、控制不住锈斑、污染严重、对人体危害大等。亚硝酸盐类防锈剂能达到良好的防锈效果，其有廉价、方便、易去除等优点。但由于其可与胺类发生反应生成致癌物而受到使用和排放的限制。亚硝酸盐不仅对人体伤害极大，且使用后在金属表面容易形成白斑，影响外观。虽然也有很多环保型水基防锈剂问世，但其防锈性能较差，尤其对于铸铁材料往往达不到工艺要求。一般水基防锈剂防锈期短，一些需要中途运输的工件大多采用高价的防锈油进行防锈处理，成本居高不下。因此，一种高效长期水性防锈剂的研究迫在眉睫。
技术实现思路
本专利技术针对现有技术的不足，提供不会影响被防锈材料表面金属光泽，使用方便、易去除，防锈期长，可达一个月以上的长期水性防锈剂及其制备方法。本专利技术通过以下技术手段实现解决上述技术问题的：一种长期水性防锈剂，包括以下质量分本文档来自技高网...

【技术保护点】
一种长期水性防锈剂，其特征在于，包括以下质量分数的原料制备：三乙醇胺15‑17份、硼酸钠2‑3份、植酸1‑2份、树脂2‑3份、叔丁基苯甲酸0.1‑0.2份、甲基苯并三氮唑1‑2份、表面活性剂0.5‑1份、去离子水71.8‑78.4份。

【技术特征摘要】
1.一种长期水性防锈剂，其特征在于，包括以下质量分数的原料制备：三乙醇胺15-17份、硼酸钠2-3份、植酸1-2份、树脂2-3份、叔丁基苯甲酸0.1-0.2份、甲基苯并三氮唑1-2份、表面活性剂0.5-1份、去离子水71.8-78.4份。2.根据权利要求所述的长期水性防锈剂，其特征在于，其中表面活性剂包括：十二烷基苯磺酸钠、十四醇聚氧乙烯醚、TA-90中的至少一种。3.根据权利要求所述...