The invention provides a window insulation film, including the main components of resin and plasticizer, viscous substance produced the film through the main components of the resin and plasticizer mixtures of the films are pasted in use; the main components of resin selected from vinyl chloride resin, ethylene vinyl acetate copolymer resin ethylene methacrylic acid copolymer resin, polyurethane resin, polyacrylic acid resin and polyester resin in one or more. The viscous substance of the invention through the main components of resin and the formation of plasticizer mixtures based on the adhesive layer, keep for a long time the film is pasted and used, at the same time the characteristics of the viscous material, a thin film after stripping no residue of the beneficial effects of stickies in a glass window.
【技术实现步骤摘要】
窗用隔热薄膜
本专利技术涉及窗用隔热薄膜
，具体来说涉及一种无需设置粘合剂层实现被粘贴使用的窗用隔热薄膜。
技术介绍
室内温度由于从窗户射入的阳光而上升。因此，窗户上需要贴一层反射或吸收阳光的薄膜，来防止室内温度上升。从而减轻空调设备的运作，并且节约能源。为了达到这样的效果而使用的窗用隔热薄膜通常通过具有较强粘性的压敏粘合剂粘贴于窗户的玻璃。
技术实现思路
值得注意的是，由于压敏粘合剂具有较强的黏性，粘贴后不易去除，故通过压敏粘合剂将薄膜粘贴于窗户，相当仰赖熟练粘贴施工技巧，避免位置偏移造成粘贴作业无法顺利进行。此外，通过压敏粘合剂实现粘贴的隔热薄膜每3～5年需要替换，压敏粘合剂的粘性不仅造成去除作业相当困难，同时存在隔热薄膜剥离后玻璃表面会残留粘合剂的问题。是以，有鉴于上述情况，本专利技术的目的在于，提供一种窗用隔热薄膜，以实现隔热薄膜容易被粘贴于窗户玻璃上，且剥离后不会在玻璃上残留粘合剂。为实现上述目的，本专利技术采取的技术方案是提供一种窗用隔热薄膜，包括主成分树脂和增塑剂，所述薄膜通过所述主成分树脂及所述增塑剂的混合物产生的粘性物质保持薄膜的被粘贴使用状态...
【技术保护点】
一种窗用隔热薄膜，其特征在于，包括主成分树脂和增塑剂，所述薄膜通过所述主成分树脂及所述增塑剂的混合物产生的粘性物质保持薄膜的被粘贴使用状态；所述主成分树脂选自氯乙烯树脂、乙烯醋酸乙烯共聚树脂、乙烯甲基丙烯酸共聚树脂、聚氨酯树脂、聚丙烯酸树脂以及聚酯树脂中的一种或多种。
【技术特征摘要】
1.一种窗用隔热薄膜，其特征在于，包括主成分树脂和增塑剂，所述薄膜通过所述主成分树脂及所述增塑剂的混合物产生的粘性物质保持薄膜的被粘贴使用状态；所述主成分树脂选自氯乙烯树脂、乙烯醋酸乙烯共聚树脂、乙烯甲基丙烯酸共聚树脂、聚氨酯树脂、聚丙烯酸树脂以及聚酯树脂中的一种或多种。2.根据权利要求1所述的窗用隔热薄膜，其特征在于：所述主成分树脂和增塑剂的配比为100重量份树脂，20～40重量份增塑剂。3.根据权利要求1或2所述的窗用隔热薄膜，其特征在于：所述增塑剂选自邻苯二甲酸酯类、己二酸酯类、偏苯三甲酸三辛酯、羧酸乙二醇酯以及磷酸甲苯酯中的一种或多种。4.根据权利要求3所述的窗用隔热薄膜，其特征在于：所述邻苯二甲酸酯类增塑剂选自邻苯二甲酸二辛酯、邻苯二甲酸二异壬酯及邻苯二甲酸二丁酯中的一种或多种。5.根据权利要求3所述的窗用隔热薄膜，其特征在于：所述己二酸酯类增塑剂选自己二酸二辛酯及己...