The invention discloses a preparation method for calcium stearate lubricant papermaking, the emulsifier aqueous solution of A stirring and heating, addition of calcium oxide, digestive reaction, preparation of calcium hydroxide emulsion; then the emulsifier B aqueous solution and mixed fatty acid stirring and heating, adding calcium hydroxide emulsion, and then in 80 to 90 DEG C for 1.5 to 2 hours, down to 60 to 70 DEG C to discharge, lubricant products. Calcium stearate lubricant provided by the invention, low viscosity, small particle size, good storage stability, preparation method provided by the invention has the advantages of simple operation, short time, low cost, and has wide application prospect and market potential.
【技术实现步骤摘要】
一种用于造纸的硬脂酸钙润滑剂的制备方法
本专利技术涉及一种用于造纸的润滑剂，尤其涉及一种用于造纸的硬脂酸钙润滑剂的制备方法。
技术介绍
随着国内造纸行业的生产规模不断扩大，涂布纸的需求量不断增加，涂布纸机的车速越来越快，这使得对涂料的润滑性能要求越来越高，这就需要在涂料中添加润滑剂。该润滑剂能起到降低涂层摩擦系数，改善涂料流变性，进而提高涂层平整度，提高成品纸光泽度的效果。由于硬脂酸是一种有机弱酸，在与碱化剂反应时，碱化剂的粒径及其粒径分布对中和反应产物的粒径有很大影响，从而影响到润滑剂的效率和储存稳定性。一般的硬脂酸钙润滑剂分散液需要使用食品级氢氧化钙作为其碱化剂，才能使得碱化剂的纯度及粒度达到要求。利用CaO制备的Ca(OH)2可用于硬脂酸钙润滑剂的制备，可以达到上述食品级氢氧化钙效果。张光华，杨飘的《初生皂法制备硬脂酸钙分散液》一文中提到：CaO在水中转化为Ca(OH)2是影响硬脂酸钙分散液性能的重要因素；其结论是，为了得到低粘度、高固含量的产品，应当延长CaO在水中的浸泡时间，使其充分转化为Ca(OH)2并形成石灰乳液；并且得出CaO的水合最佳时间为72～...
【技术保护点】
一种用于造纸的硬脂酸钙润滑剂的制备方法，其特征在于，包括以下步骤：(1)先将乳化剂A水溶液搅拌加热至40～60℃，再向其中加入氧化钙，搅拌，进行消化反应0.5～1小时，制得氢氧化钙乳液；(2)将乳化剂B水溶液和混合脂肪酸搅拌加热至75～90℃，再加入步骤(1)所制得的氢氧化钙乳液，逐渐加快搅拌速率，然后在80～90℃下反应1.5～2小时，降温到60～70℃出料；其中，所述混合脂肪酸为硬脂酸和不饱和脂肪酸的混合物；其中，各反应物料的质量份配比如下：
【技术特征摘要】
1.一种用于造纸的硬脂酸钙润滑剂的制备方法，其特征在于，包括以下步骤：(1)先将乳化剂A水溶液搅拌加热至40～60℃，再向其中加入氧化钙，搅拌，进行消化反应0.5～1小时，制得氢氧化钙乳液；(2)将乳化剂B水溶液和混合脂肪酸搅拌加热至75～90℃，再加入步骤(1)所制得的氢氧化钙乳液，逐渐加快搅拌速率，然后在80～90℃下反应1.5～2小时，降温到60～70℃出料；其中，所述混合脂肪酸为硬脂酸和不饱和脂肪酸的混合物；其中，各反应物料的质量份配比如下：2.根据权利要求1所述的制备方法，其特征在于，所述乳化剂A为脂肪酸甲酯乙氧基化物的磺酸盐或/和壬基酚聚氧乙烯醚磺酸钠。3.根据权利要求1所述的制备方法，其特征在于，所述乳化剂B选自以下任...
【专利技术属性】
技术研发人员：施晓旦，于广伟，王虎，金霞朝，
申请(专利权)人：上海东升新材料有限公司，
类型：发明
国别省市：上海,31