The invention discloses a low surface treatment of epoxy resin paint, which comprises the following components and weight: group A: epoxy resin 20 ~ 35, 1 ~ 2 dispersant and anti settling agent 1 ~ 3, 5 ~ 10 of titanium dioxide and talc powder 15 ~ 25, 3 ~ 8, zinc phosphate tripolyphosphate from 5 to 15, aluminum Benzenemethanol 3 ~ 10, 0.3 ~ 1 defoaming agent and xylene 5 ~ 15; group B: modified amine curing agent 60 ~ 75, 2 ~ 5 accelerator and mixed solvent from 25 to 40; the quality and the component B is 5:1. The curing agent of the present invention using hydrogenated petroleum resin modified curing agent can improve wet permeability, rust inside can drive the liquid paint to penetrate into the porous, curing reaction after the film formation is tightly wrapped to prevent rust rust layer, further development. The modified curing agent introduced flexible segments to improve the flexibility and adhesion of the films. At the same time, the moisture tolerance is increased and the corrosion resistance of the film is improved.
【技术实现步骤摘要】
一种低表面处理环氧树脂漆及其制备方法
本专利技术属于防腐涂料领域，具体涉及一种低表面处理环氧树脂漆。
技术介绍
现代工业生产生活中，在防止钢铁腐蚀生锈的各种方法中，涂料涂装防腐技术仍是最为经济有效，且获得广泛应用的方法。以往对金属表面进行涂装防腐，必须先对金属表面进行严格的前处理，如喷砂，才能得到较好的防腐效果。但喷砂工艺造价高，污染大，因此人们开发出低表面处理涂料，即使用手工或动力工具打磨金属表面，在除锈不完全或达不到Sa2级以上，或者潮湿环境下能够涂覆到金属表面，且具有良好的附着力和防腐蚀性能的涂料。目前国内外已经有类似产品，如含单宁酸锈转化剂，或酮亚胺改性固化剂或腰果酚型酚醛胺等类型的低表面处理环氧漆，但都存在不足，单宁酸类锈转化型对酸与锈蚀的合理匹配难以控制，易造成锈蚀转化不足或酸过量致钢铁腐蚀；酮亚胺类固化剂属潮气固化型漆，水分容易首先在漆膜表面发生反应形成封闭表面，造成漆膜内部固化不充分；酚醛胺型固化的漆膜通常刚性有余，韧性不足。本专利技术含高效润湿渗透性物质，可快速润湿底材，并渗透进锈层内部并包裹阻止锈蚀发展，所以可直接涂覆于除锈不彻底，或潮湿表面，...
【技术保护点】
一种低表面处理环氧树脂漆，其特征在于，包括以下组分和重量份数：甲组分：
【技术特征摘要】
1.一种低表面处理环氧树脂漆，其特征在于，包括以下组分和重量份数：甲组分：乙组分：改性胺树脂60～75；促进剂2～5；混合溶剂20～40；所述甲组分与所述乙组分的质量比为5：1。2.如权利要求1所述的一种低表面处理环氧树脂漆，其特征在于，所述环氧树脂为低分子量的双酚A环氧树脂。3.如权利要求1所述的一种低表面处理环氧树脂漆，其特征在于，所述流变剂为酰胺蜡粉。4.如权利要求1所述的一种低表面处理环氧树脂漆，其特征在于，所述改性胺树脂为聚酰胺树脂与加氢石油树脂搅拌混合均匀后，密封放置24h得到的。5.如权利要求1所述的一种低表面处理环氧树脂漆，其特征在于，所述促进剂为2，4，6-三(二甲氨...
【专利技术属性】
技术研发人员：卢常巧，
申请(专利权)人：上海古象化工科技发展有限公司，
类型：发明
国别省市：上海,31
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。