The invention discloses a self thermal insulation wall of lightweight concrete, including ceramsite, perlite, 20 mesh to 30 mesh 10 mesh to 90 mesh of perlite, cement, water, admixture of lightweight concrete in the lightweight concrete, the unit weight of the components in weight percentage are: the content of ceramsite 28% 33%, 20 mesh to 30 mesh of the perlite content is 3% 4%, 10 mesh to 90 mesh of the perlite content is 4% 6%, the cement content is 23% 30%, the water content is 26.6% 28%, the content of admixture is 2% 4%, the admixture for polymer adhesive. The invention adopts the new formula material, and the concrete wall made by the invention can ensure the wall to have the qualified heat preservation performance and has the qualified strength.
【技术实现步骤摘要】
自保温墙体轻质混凝土
本专利技术涉及建筑新材料
，尤其是涉及一种自保温墙体轻质混凝土。
技术介绍
随着社会的发展，世界能源逐渐减少，目前能够减缓能源使用的方式就是推广高效的节能产品。与之适应的是，现在在建筑材料中已经提出大量采用能够实现自保温的混凝土预制墙体，但是，除了保温，作为建筑结构的保温墙体，也需要有足够的强度来保证建筑物的强度，而现阶段的保温墙体能够达到保温要求的无法达到强度要求，能够达到强度要求的无法达到保温要求。
技术实现思路
本专利技术是为了解决现有保温墙体在保温性能与强度要求之间无法兼得的问题，提供一种采用新配方材料，能够在保证墙体具有合格保温性能的同时，具有合格的强度的自保温墙体轻质混凝土。为了实现上述目的，本专利技术采用以下技术方案：自保温墙体轻质混凝土，所述的轻质混凝土中包含陶粒、20目至30目珍珠岩、10目至90目珍珠岩、水泥、水、外掺剂，所述单位重量的轻质混凝土中各组分重量比例分别是：所述的陶粒含量为28％-33％，所述的20目至30目珍珠岩含量为3％-4％，所述的10目至90目珍珠岩含量为4％-6％，所述的水泥含量为23％-30％，所...
【技术保护点】
一种自保温墙体轻质混凝土，其特征在于，所述的轻质混凝土中包含陶粒、20目至30目珍珠岩、10目至90目珍珠岩、水泥、水、外掺剂，所述单位重量的轻质混凝土中各组分重量比例分别是：所述的陶粒含量为28％‑33％，所述的20目至30目珍珠岩含量为3％‑4％，所述的10目至90目珍珠岩含量为4％‑6％，所述的水泥含量为23％‑30％，所述的水含量为26.6％‑28％，所述的外掺剂含量为2％‑4％，所述的外掺剂为高分子胶。
【技术特征摘要】
1.一种自保温墙体轻质混凝土，其特征在于，所述的轻质混凝土中包含陶粒、20目至30目珍珠岩、10目至90目珍珠岩、水泥、水、外掺剂，所述单位重量的轻质混凝土中各组分重量比例分别是：所述的陶粒含量为28％-33％，所述的20目至30目珍珠岩含量为3％-4％，所述的10目至90目珍珠岩含量为4％-6％，所述的水泥含量为23％-30％，所述的水含量为26.6％-28％，所...