The present invention discloses thermal insulation materials for buildings, which belongs to the technical field of thermal insulation material, which comprises the following raw materials in weight portion: 14 fluorocarbon emulsion 18 copies, 10 copies, 8 perlite 2 sepiolite powder 6, aluminum silicate fiber and glass fiber 2 4 1 3 1, asbestos 2 a 3, bentonite 5, nano hollow ceramic beads 2 5 copies, 1 copies, 0.5 polyacrylamide Suo Jiaji 1 cellulose 2, Zinc Oxide 2 4 copies, 3 copies, 1 penetrant hydrophober 0.5 1 copies, 0.8 copies, antioxidant 0.5 water 45 50 preparation method; the invention also discloses a thermal insulation material for building; the invention has the advantages of simple preparation, use for a long time, has better heat insulation ability.
【技术实现步骤摘要】
一种建筑用隔热保温材料及其制备方法
本专利技术涉及保温材料
，具体的说，涉及了一种建筑用隔热保温材料及其制备方法。
技术介绍
建筑节能将是21世纪中国建筑事业发展的一个重点，据有关部门的预测，建筑节能约为全国总能耗的20％，而建筑材料在使用过程中的能耗占有很大比例。为了减少建筑物的散热损失，采用保温性能良好的建筑材料是一项重要的措施。现在一般外墙或内墙都是用泡沫或泡沫板之类的易燃品做保温材料，在保温过程中存在严重的火灾隐患，引起有关部门高度关切，我国提出了建筑保温材料的新标准，规定民用建筑的楼梯间隔墙、公共建筑采暖分区的隔墙、高层建筑的电梯井墙、实现采暖分户计量收费的居住建筑分户墙、地板热辐射采暖的楼板，都应采用A级保温材料来提高其保温、隔热、阻燃性能。保温材料一般是指导热系数小于或等于0.2的材料。保温材料发展很快，在工业和建筑中采用良好的保温技术与材料，往往可以起到事半功倍的效果。建筑中每使用一吨矿物棉绝热制品，一年可节约一吨石油；传统的保温隔热材料是以提高气相空隙率，降低导热系数和传导系数为主。纤维类保温材料在使用环境中要使对流传热和辐射传热升高，必须...
【技术保护点】
一种建筑用隔热保温材料，其特征在于：包括以下重量份的原料：氟碳乳液14‑18份、珍珠岩8‑10份、海泡石粉2‑6份、硅酸铝纤维2‑4份、玻璃纤维1‑3份、石棉1‑2份、膨润土3‑5份、纳米空心陶瓷微珠2‑5份、聚丙烯酰胺0.5‑1份、羧甲基纤维素1‑2份、氧化锌2‑4份、渗透剂1‑3份、憎水剂0.5‑1份、防老剂0.5‑0.8份、水45‑50份。
【技术特征摘要】
1.一种建筑用隔热保温材料，其特征在于：包括以下重量份的原料：氟碳乳液14-18份、珍珠岩8-10份、海泡石粉2-6份、硅酸铝纤维2-4份、玻璃纤维1-3份、石棉1-2份、膨润土3-5份、纳米空心陶瓷微珠2-5份、聚丙烯酰胺0.5-1份、羧甲基纤维素1-2份、氧化锌2-4份、渗透剂1-3份、憎水剂0.5-1份、防老剂0.5-0.8份、水45-50份。2.根据权利要求1所述的建筑用隔热保温材料，其特征在于：珍珠岩和海泡石粉的目数为200目，氧化锌的目数为170目。3.根据权利要求1所述的建筑用隔热保温材料，其特征在于：硅酸铝纤维的长度为0.2-1mm，直径为0.1-0.5mm；玻璃纤维的长度为0.1-0.5mm，直径为0.05-0.08mm。4.根据权利要求1所述...
【专利技术属性】
技术研发人员：徐仙峰，
申请(专利权)人：合肥择浚电气设备有限公司，
类型：发明
国别省市：安徽,34