The invention discloses a high density incombustible decorative plate, the plate will roll by 600 to 1200 tons of press cold pressing at room temperature 1 ~ 2min, and then 35 to 50 DEG C in the maintenance room standing for 2 to 5 hours, the prepared high density incombustible decorative plate. According to the method of the invention can significantly improve the density of decorative plate flatness, reduce the thickness error of decorative plates, decorative plate with and without cold pressing step compared to the whole plate thickness error by 0.5 ~ 1mm error is reduced to less than 0.1mm, and the apparent density can be increased by more than 20%.
【技术实现步骤摘要】
防火型装饰板
本专利技术涉及一种防火型装饰板。
技术介绍
在建筑装饰、家具制造中，装饰板被大量应用。现有的装饰板主要以木质为主，其防火性能差。对不燃装饰板的需求很大。而且现有的装饰板强度通常不高，达不到某些特殊工艺要求。
技术实现思路
为了克服现有装饰板的上述不足，本专利技术提供一种防火性能好，强度高的高密度不燃装饰板，本专利技术采取的技术方案是：A、在常温常压下将氧化镁粉末、秸秆粉末、膨胀珍珠岩粉末混合均匀后倒入密封釜中；再加入2～10mol/L、pH值调至6.5～9.5的氯化镁溶液搅拌均匀，制得浆料；在制板机最下层铺设一层无纺布，在所述无纺布上方再铺设1～5层玻璃纤维布，所得浆料通过密封输送管输送到制板机下料口，涂覆在1～5层玻璃纤维布的表面上，所述1～5层玻璃纤维布的表面上涂敷浆料后，再铺设一层无纺布，然后同步辊压成板材；B、步骤A所得板材用600～1200吨压力机在室温下冷压1～2min，然后送入35～50℃的养护房内静置2～5小时，制备得到高密度不燃装饰板；所述的高密度不燃装饰板厚度控制在3～20mm；所述的氯化镁溶液中的氯化镁、氧化镁粉末、秸秆粉末、膨胀珍...
【技术保护点】
一种防火型装饰板，其特征在于所述高密度不燃装饰板按以下方法制备得到：A、在常温常压下将氧化镁粉末、秸秆粉末、膨胀珍珠岩粉末混合均匀后倒入密封釜中；再加入2 ～ 10mol/L、pH 值调至6.5 ～ 9.5 的氯化镁溶液搅拌均匀，制得浆料；在制板机最下层铺设一层无纺布，在所述无纺布上方再铺设1 ～ 5 层玻璃纤维布，所得浆料通过密封输送管输送到制板机下料口，涂覆在1 ～ 5 层玻璃纤维布的表面上，所述1 ～ 5 层玻璃纤维布的表面上涂敷浆料后，再铺设一层无纺布，然后同步辊压成板材；B、步骤A 所得板材用600 ～ 1200 吨压力机在室温下冷压1 ～ 2min，然后送入35...
【技术特征摘要】
1.一种防火型装饰板，其特征在于所述高密度不燃装饰板按以下方法制备得到：A、在常温常压下将氧化镁粉末、秸秆粉末、膨胀珍珠岩粉末混合均匀后倒入密封釜中；再加入2～10mol/L、pH值调至6.5～9.5的氯化镁溶液搅拌均匀，制得浆料；在制板机最下层铺设一层无纺布，在所述无纺布上方再铺设1～5层玻璃纤维布，所得浆料通过密封输送管输送到制板机下料口，涂覆在1～5层玻璃纤维布的表面上，所述1～5层玻璃纤维布的表面上涂敷浆料后，再铺设一层无纺布，然后同步辊压成板材；B、步骤A所得板材用600～1200吨压力机在室温下冷压1～2min，然后送入35～50℃的养护房内静置2～5小时，制备得到高密度不燃装饰板；所述的高密度不燃装饰板厚度控制在3～20mm；所述的氯化镁溶液中的氯化镁、氧化镁粉末、秸秆粉末、膨胀珍珠岩粉末质量比为1∶0.4～2∶0.4～2∶0.1～1。2.如权利要求1所述的防火型装饰板，其特征在于所述的氯化镁溶液中的氯化镁、氧化镁...