一种住宅隔音楼板及其制作方法技术

一种住宅隔音楼板，包括钢筋混凝土板面层、上层玻璃纤维织物复合材料、聚丙烯树脂蜂窝材料和下层玻璃纤维织物复合材料；本发明专利技术采用了两次成型的方法将内外层与芯材料胶结在一起固化成型，调节了两次粘结压力的大小，并且使用两层不同厚度的玻璃纤维织物复合材料，与聚丙烯树脂蜂窝材料一起形成了一种非对称的结构，经实验比较这种结构不仅大幅度提高了楼板结构的刚度，并同时提升了楼板的隔音性能。

Residential soundproof floorslab and manufacturing method thereof

A residential soundproof floor, including reinforced concrete layer, the upper glass fiber fabric composite material, polypropylene resin honeycomb material and the lower glass fiber fabric composite material; the invention adopts two molding method inside and outside layer and core material cemented together into curing type, adjusting two bond force and use the two layers with different thickness of glass fiber fabric composites and polypropylene resin honeycomb material together form an asymmetric structure, the experimental comparison of the structure not only improves the rigidity of the floor structure, and simultaneously enhance the sound insulation performance of the floor.

【技术实现步骤摘要】
一种住宅隔音楼板及其制作方法
本专利技术属于建筑用楼板结构
，具体涉及一种住宅隔音楼板及其制作方法。
技术介绍
住宅是居民生活休息的主要场所，本应是一个清静舒适的地方。然而随着社会经济、交通、工业的发展及自然环境的破坏，城市的噪声污染越来越严重，居住建筑外围的噪声主要来自交通噪声、施工噪声、生产企业噪声和室外社会生活噪声。调查显示，城市高层住宅由于楼板和轻质分户墙隔声性能太差，有80%以上的高层住宅隔声能力达不到国家规范要求。导致住宅隔声效果不好的原因是多方面的，其中最主要的原因是轻质墙体的不合理应用。近几年我国新型墙材有了很大的发展，例如夹层结构的墙体，通常是由比较薄的面板和比较厚的芯子胶结而成，具有质量轻、强度大、隔音隔热等优点。在夹层结构中，使用低密度夹心材料来增加层合板的厚度，从而达到提高材料刚度的目的。本专利技术中利用蜂窝状芯子结构，并配合非对称结构的双层玻璃纤维织物复合材料的使用，在重量增加很少的前提下，大幅度提高了结构的刚度，并同时提升了楼板的隔音性能。专利CN106273802A中提供了一种复合夹层楼板沿竖直方向分为三层，从上依次为钢筋混凝土板面层、聚苯乙烯泡沫本文档来自技高网...

【技术保护点】
一种住宅隔音楼板，其特征在于，包括钢筋混凝土板面层（1）、上层玻璃纤维织物复合材料（2）、聚丙烯树脂蜂窝材料（3）和下层玻璃纤维织物复合材料（4）。

【技术特征摘要】
1.一种住宅隔音楼板，其特征在于，包括钢筋混凝土板面层（1）、上层玻璃纤维织物复合材料（2）、聚丙烯树脂蜂窝材料（3）和下层玻璃纤维织物复合材料（4）。2.一种权利要求1中所述的一种住宅隔音楼板的的制作方法，其特征在于：1）将钢筋混凝土板面层（1）和上层玻璃纤维织物复合材料（2）分别成型后使用粘结剂胶合固化，控制压力为0.01-0.08MPa；2）将聚丙烯树脂蜂窝材料（3）和下层玻璃纤维织物复合材料（4）与钢筋混凝土板面层（1）、上层玻璃纤维织物复合材料（2）胶合板继续使用粘合剂胶结固化，调节压力为0.9KPa，控制温度在135℃，保持30min；3）在30min内下降至90℃，...

【专利技术属性】
技术研发人员：张俊娥，钱冬梅，
申请(专利权)人：滁州筑梦绿色建筑有限公司，
类型：发明
国别省市：安徽,34