无水压入泥浆制造技术

本发明专利技术涉及无水压入泥浆，由以下重量百分比的组分组成：0～1mm矾土20.5～30.6%、粒度为200目的矾土25.7～28.6%、铝酸盐水泥4.7～6.4%、碳粉2.4～3.3%、树脂27.9～30.5%、结合剂8.7～10.7%；本发明专利技术的优点：通过上述组分混合制成的无水压入泥浆，具有良好的导热系数，提高热效率，高温下收缩性能小，硬化后形成坚实的整体，大大提高密闭性，流动性能好，能满足快速烘烤，可实现立即投产使用。

Waterless entry mud

The present invention relates to water pressure into the mud, consists of the following components in weight percentage: 0 ~ 1mm, 20.5 ~ 30.6% alumina particle size of 200 to 25.7 ~ 28.6%, alumina aluminate cement 4.7 ~ 6.4%, 2.4 ~ 3.3%, toner resin 27.9 ~ 30.5%, 8.7 ~ 10.7% bond; the invention has the advantages that the pressure into the mud by the components are mixed with water, good thermal conductivity, improve the thermal efficiency, high temperature shrinkage of small, hardened to form solid overall, greatly improve the tightness, good fluidity, can meet the fast curing, can be put into operation immediately to use.

【技术实现步骤摘要】

本专利技术涉及无水压入泥浆。
技术介绍
无水压入泥浆用于填充炉壳与冷却壁之间以及炉底封板下部间隙，固化后形成坚实、致密的整体，杜绝了高炉采用水质灌浆料在高炉投产后对炭质炉衬的破坏，现有的无水压入泥浆需要长时间烘烤，效率低，高温下收缩比例大，形成不了整体，使用效果一般，造成频繁检修。
技术实现思路
本专利技术要解决的技术问题是现有的无水压入泥浆存在效率低，使用效果差，高温下收缩比例大，从而提供无水压入泥浆。为了解决上述技术问题，本专利技术是通过以下技术方案实现的：无水压入泥浆，由以下重量百分比的组分组成：0～1mm矾土20.5～30.6%、粒度为200目的矾土25.7～28.6%、铝酸盐水泥4.7～6.4%、碳粉2.4～3.3%、树脂27.9～30.5%、结合剂8.7～10.7%。优选的，由以下重量百分比的组分组成：0～1mm矾土30.6%、粒度为200目的矾土25.7%、铝酸盐水泥4.7%、碳粉2.4%、树脂27.9%、结合剂8.7%，通过上述质量百分比组分混本文档来自技高网...

【技术保护点】
无水压入泥浆，其特征在于：由以下重量百分比的组分组成：0～1mm矾土20.5～30.6%、粒度为200目的矾土25.7～28.6%、铝酸盐水泥4.7～6.4%、碳粉2.4～3.3%、树脂27.9～30.5%、结合剂8.7～10.7%。

【技术特征摘要】
1.无水压入泥浆，其特征在于：由以下重量百分比的组分组成：0～1mm矾土
20.5～30.6%、粒度为200目的矾土25.7～28.6%、铝酸盐水泥4.7～6.4%、
碳粉2.4～3.3%、树脂27.9～30.5%、结合剂8.7～10.7%。
2.根据权利要求1所述的无水压入泥浆，其特征在于：由以下重量百分比的组
分组成：0～1mm矾土30.6%、粒度为200目的矾土25.7%、铝酸盐水泥4.7%、
碳粉2.4%、树脂27.9%、结合剂8.7%。
3.根据权利要求1所述的无水压入泥浆，其特征在于：由以下重量百分比的组
分组成：0～1mm矾土24%、粒度为2...

【专利技术属性】
技术研发人员：李开胜，
申请(专利权)人：长兴明晟冶金炉料有限公司，
类型：发明
国别省市：浙江;33