The present invention relates to a tundish coating, consists of the following components in weight percentage: 2 ~ 3mm ~ 13.7% and 1 ~ 11.8 magnesia magnesia 2mm 13.5 ~ 15.6%, 0.5 ~ 1mm ~ 16.1% and 0 ~ 13.6 magnesia magnesia 0.5mm 15.9 ~ 17.8%, 180 to 30 ~ 40%, magnesia silica powder is 2.75 ~ 3.25%, 0.26 Guangxi mud ~ 0.35%, 0.27 ~ 0.36% of calcium lignosulfonate and sodium tripolyphosphate 0.48 ~ 0.67%, 0.99 ~ 1.38%, the paper fiber alumina cement 0.45 ~ 0.64%, 0 ~ 0.15% metal powder; the invention has the advantages that the coating material has good heat preservation performance and service life of the components of intermediate mixes, can adapt to the variety of pouring changes of casting steel and cast steel with a yield, reduce the thermal conductivity of coating, improve the coating properties.
【技术实现步骤摘要】
本专利技术涉及中间包涂料。
技术介绍
在钢水供应十分充足的建筑钢等品种的生产中，特别是在水口能在线快速更换的条件下，需要的中间包具有使用寿命长等特点，现有的中间包通过高性能的镁质预制件、镁质涂料及镁铝铬质涂料等原料来提高使用寿命，随着中间包冶金技术的发展，优质钢和特殊钢的比例增加，受浇铸钢的品种变化和浇铸同一种钢的产量限制导致对中间包的使用寿命要求不高，而无法满足浇注钢质量，需要对中间包具有良好的保温效果。
技术实现思路
本专利技术要解决的技术问题现有中间包的保温效果差导致浇注钢质量差，从而提供中间包涂料。为了解决上述技术问题，本专利技术是通过以下技术方案实现的：中间包涂料，由以下重量百分比的组分组成：2～3mm镁砂11.8～13.7%、1～2mm镁砂13.5～15.6%、0.5～1mm镁砂13.6～16.1%、0～0.5mm镁砂15.9～17.8%、粒度为180目的镁砂30～40%、硅微粉2.75～3.25%、广西泥0.26～0.35%、木质素磺...
【技术保护点】
中间包涂料，其特征在于：由以下重量百分比的组分组成：2～3mm镁砂11.8～13.7%、1～2mm镁砂13.5～15.6%、0.5～1mm镁砂13.6～16.1%、0～0.5mm镁砂15.9～17.8%、粒度为180目的镁砂30～40%、硅微粉2.75～3.25%、广西泥0.26～0.35%、木质素磺酸钙0.27～0.36%、三聚磷酸钠0.48～0.67%、纸纤维0.99～1.38%、矾土水泥0.45～0.64%、金属铝粉0～0.15%。
【技术特征摘要】
1.中间包涂料，其特征在于：由以下重量百分比的组分组成：2～3mm镁砂11.8～
13.7%、1～2mm镁砂13.5～15.6%、0.5～1mm镁砂13.6～16.1%、0～0.5mm
镁砂15.9～17.8%、粒度为180目的镁砂30～40%、硅微粉2.75～3.25%、广
西泥0.26～0.35%、木质素磺酸钙0.27～0.36%、三聚磷酸钠0.48～0.67%、
纸纤维0.99～1.38%、矾土水泥0.45～0.64%、金属铝粉0～0.15%。
2.根据权利要求1所述的中间包涂料，其特征在于：由以下重量百分比的组分
组成：2～3mm镁砂13.7%、1～2mm镁砂15.6%、0.5～1mm镁砂16.1%、0～
0.5mm镁砂17.8%、粒度为180目的镁砂30%、硅微粉3.25%、广西泥0.35%、
木质素磺酸钙0.36%、三聚磷酸钠0.67%、纸纤维1.38%、矾土水泥0.64%、
金属铝...