一种具有良好可见光响应的二维Bi12TiO20纳米片的制备方法技术

本发明专利技术属于化学材料制备技术领域，提供一种具有良好可见光响应的二维Bi12TiO20纳米片的制备方法。本发明专利技术通过直接煅烧法一步制成二维片状Bi12TiO20；并通过光催化降解染料实验证明所制备二维Bi12TiO20纳米片光催化剂具有良好的光催化活性，性能优于传统块状Bi12TiO20；本发明专利技术制备工艺简便，制备成本低，效率高，实用性强，易于进行大规模生产，具备良好的经济效益和环保效益。

Method for preparing two-dimensional Bi12TiO20 nano film with good visible light response

The invention belongs to the technical field of chemical material preparation, and provides a method for preparing two-dimensional Bi12TiO20 nano film with good visible light response. The present invention by direct calcination step into two-dimensional sheet Bi12TiO20; and through the proof of photocatalytic degradation of dyes were prepared two-dimensional nano Bi12TiO20 photocatalyst has excellent photocatalytic activity, performance is better than the traditional block Bi12TiO20; the invention has the advantages of simple preparation process, low preparation cost, high efficiency, strong practicability, easy to carry mass production, good economic benefits and environmental benefits.

【技术实现步骤摘要】

本专利技术属于化学材料制备
，提供一种具有良好可见光响应的二维片状Bi12TiO20材料的制备方法。
技术介绍
随着现代工农业的发展,水环境污染越来越严重,水体中大量有机污染物严重威胁着人类自身乃至动植物的健康生长，治理水污染迫在眉睫。光催化技术是一种高级氧化技术(AOPs),近年来在有机废水特别是在高浓度、难降解废水的治理中受到广泛的关注。其中，二维材料由于其更短的光生电子空穴传输距离，优异的载流子传输效率和更多的反应位点，一直是近几年研究的热点。也因为这些优点，这种结构的材料有着更强的光催化活性。Bi2O3和TiO2复合可形成具有多种晶相结构的复合氧化物:Bi4Ti3O12，Bi2Ti2O7，Bi2Ti4O11，Bi12TiO20，Bi20TiO32等，通称为钛酸铋化合物。钛酸铋化合物有着特殊的晶体结构和电子结构,在它们的结构中均存在TiO6八面体或TiO4四面体,而与之相连接的BiOn多面体中存在因拥有6s2孤对电子对而具有立体活性的Bi3+离子,这就使得其具有很好的光催化活性。Xu等(Acta.Chimica.Sinica,2005,63(1),5)将一定摩尔比的硝酸本文档来自技高网...

【技术保护点】
一种具有良好可见光响应的二维Bi12TiO20纳米片的制备方法，其特征在于，包括以下步骤：(1)称取一定量的氧化铋，P25钛白粉，氯化钠，氯化钾于研钵中，研磨均匀；(2)将步骤(1)研磨后的粉末转移到石英舟中，于管式炉中煅烧，制得二维片状Bi12TiO20。

【技术特征摘要】
1.一种具有良好可见光响应的二维Bi12TiO20纳米片的制备方法，其特征在于，包括以下步骤：(1)称取一定量的氧化铋，P25钛白粉，氯化钠，氯化钾于研钵中，研磨均匀；(2)将步骤(1)研磨后的粉末转移到石英舟中，于管式炉中煅烧，制得二维片状Bi12TiO20。2.根据权利要求1所述的一种具有良好可见光响应的二...

【专利技术属性】
技术研发人员：钱坤，谢吉民，夏莉，魏巍，姜志锋，孙伟，吕霞，
申请(专利权)人：江苏大学，
类型：发明
国别省市：江苏;32